ABS LNP™ STAT-KON™ A3000 BK8115 SABIC INNOVATIVE US
198
- Unit Price:US$ 3,120 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Antistatic
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.40 % | |
| ASTM D955 | 0.50 % | ||
| Water absorption rate | ASTM D570 | 1.1 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2060 Mpa | |
| ISO 527-2/1 | 2010 Mpa | ||
| tensile strength | ASTM D638 | 39.0 Mpa | |
| ISO 527-2/5 | 38.0 Mpa | ||
| ASTM D638 | 36.0 Mpa | ||
| ISO 527-2/5 | 31.0 Mpa | ||
| elongation | ASTM D638 | 3.1 % | |
| ISO 527-2/5 | 3.0 % | ||
| ASTM D638 | 6.0 % | ||
| ISO 527-2/5 | 24 % | ||
| Flexural modulus | ASTM D790 | 2090 Mpa | |
| ISO 178 | 1980 Mpa | ||
| bending strength | ISO 178 | 59.0 Mpa | |
| ASTM D790 | 65.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 无断裂 | |
| Dart impact | ASTM D3763 | 32.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+9 - 1.0E+11 ohms |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 70 to 80 °C | ||
| drying time | 4.0 hr | ||
| Suggested maximum moisture content | 0.050 to 0.10 % | ||
| Temperature at the rear of the barrel | 180 to 195 °C | ||
| Temperature in the middle of the barrel | 195 to 205 °C | ||
| Temperature at the front of the material cylinder | 205 to 215 °C | ||
| Processing (melt) temperature | 200 to 210 °C | ||
| Temperature | 10 to 50 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| screw speed | 30 to 60 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 88.0 °C | |
| ISO 75-2/Bf | 91.0 °C | ||
| ASTM D648 | 76.0 °C | ||
| ISO 75-2/Af | 76.0 °C | ||
| Linear coefficient of thermal expansion | ASTM E831 | 9.3E-5 cm/cm/°C | |
| ISO 11359-2 | 9.3E-5 cm/cm/°C | ||
| ASTM E831 | 1.0E-4 cm/cm/°C | ||
| ISO 11359-2 | 1.0E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.