Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS A3000 BK8115 SABIC INNOVATIVE US
LNP™ STAT-KON™
--
Antistatic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 BK8115 |
|---|---|---|---|
| 23°C | ASTM D4812, ISO 180/1U | 无断裂 | |
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 32.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 BK8115 |
|---|---|---|---|
| Bending stress | -- 5, 6 | ISO 178 | 59.0 Mpa |
| Flexural modulus | -- 5 | ISO 178 | 1980 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 31.0 Mpa |
| elongation | 屈服 3 | ASTM D638 | 3.1 % |
| Tensile modulus | -- 2 | ASTM D638 | 2060 Mpa |
| tensile strength | 屈服 3 | ASTM D638 | 39.0 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 3.0 % |
| Bending stress | 断裂, 50.0 mm 跨距 4 | ASTM D790 | 65.0 Mpa |
| Flexural modulus | 50.0 mm 跨距 4 | ASTM D790 | 2090 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 38.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2010 Mpa |
| elongation | 断裂 3 | ASTM D638 | 6.0 % |
| tensile strength | 断裂 3 | ASTM D638 | 36.0 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 24 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 BK8115 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+9 到 1.0E+11 ohms |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 BK8115 |
|---|---|---|---|
| Shrinkage rate | 流动 : 24小时 | ASTM D955 | 0.40 % |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 1.1 % |
| Shrinkage rate | 横向流动 : 24小时 | ASTM D955 | 0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 BK8115 |
|---|---|---|---|
| 横向 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| 流动 : 23 到 60°C | ISO 11359-2 | 9.3E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 1.0E-4 cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 76.0 °C |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Bf | 91.0 °C | |
| 流动 : -40 到 40°C | ASTM E831 | 9.3E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 88.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 76.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 BK8115 |
|---|---|---|---|
| Temperature | 10 到 50 °C | ||
| screw speed | 30 到 60 rpm | ||
| Temperature at the rear of the barrel | 180 到 195 °C | ||
| Processing (melt) temperature | 200 到 210 °C | ||
| Back pressure | 0.200 到 0.300 Mpa | ||
| drying temperature | 70 到 80 °C | ||
| Temperature at the front of the material cylinder | 205 到 215 °C | ||
| drying time | 4.0 hr | ||
| Suggested maximum moisture content | 0.050 到 0.10 % | ||
| Temperature in the middle of the barrel | 195 到 205 °C |