PC TARFLON™ AZ1900T IDEMITSU JAPAN

Unit Price:US$ 6,740 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Jiantou Plastic Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Automotive Applications｜Home appliance components
Color:--
Grade:High liquidity level

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity		ISO 13468-1	85.0to89.0	%
other	Test Condition	Test Method	Test Result	Test Unit
characteristic			高流动型
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	V-0
ISO			>PC<
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	90.0	Mpa
Bending modulus		ISO 178	2300	Mpa
Nominal tensile fracture strain		ISO 527-2	70	%
tensile strength	Yield	ISO 527-2	65.0	Mpa
Charpy Notched Impact Strength		ISO 179	65	kJ/m²
bending strength		ISO 178	90	Mpa
Bending modulus		ISO 178	2300	Mpa
Elongation at Break		ISO 527-2	70	%
tensile strength	Yield	ISO 527-2	65	Mpa
Elongation at Break		ASTM D638/ISO 527	92	%
Tensile modulus		ASTM D638/ISO 527	2300	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	68	kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	80	kg·cm/cm(J/M)ft·lb/in
elongation		ASTM D638/ISO 527	64	%
Bending modulus		ASTM D790/ISO 178	2400	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	92	%
tensile strength	Yield	ISO 527-2	65.0	Mpa
Nominal tensile fracture strain		ISO 527-2	95	%
bending strength		ISO 178	90.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature at the rear of the barrel			260 to 300	°C
Temperature in the middle of the barrel			260 to 300	°C
Temperature at the front of the material cylinder			260 to 300	°C
Mold temperature			80 to 120	°C
drying temperature			120	°C
drying time			5.0 to 8.0	hr
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	4.00 mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	1.50 mm	UL 94	V-0
Linear coefficient of thermal expansion		ASTM D696	0.000065	cm/cm/℃
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	125	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	140	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.5E-05	cm/cm/°C
RTI Elec		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
RTI Str		UL 746	80.0	°C
Combustibility (rate)		UL 94	V-0/1.5mm
Hot deformation temperature	HDT	ASTM D648/ISO 75	131	℃（℉）
RTI		UL 746	80.0	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	125	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	6.5E-5	cm/cm/°C
RTI Elec		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.23	%
Shrinkage rate	MD:2.00mm	Internal Method	0.50-0.70	%
Shrinkage rate	Shrinkage rate	TD:2.00mm	Internal Method	0.50-0.70	%
Spiral flow length		Internal Method	48.0	CM
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	5.00	cm3/10min
Water absorption rate	Equilibrium, 23℃, 50% RH	ISO 62	0.23	%
Shrinkage rate	MD: 2.00 mm	Internal Method	0.5-0.7	%
Shrinkage rate	Shrinkage rate	TD	Internal Method	0.5-0.7	%
Melt Volume Flow Rate (MVR)	MVR	ISO 1133	5	cm3/10min
Shrinkage rate	横向Flow : 2.00 mm	Internal Method	0.50 - 0.70	%
Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	Internal Method	0.50 - 0.70	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.23	%
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	18.0	cm3/10min
Spiral flow length		Internal Method	29.0	CM
density		ASTM D792/ISO 1183	1.20
Shrinkage rate		ASTM D955	0.5-0.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	1 MHz	IEC 60250	2.85
Dielectric strength		IEC 60243-1	30	KV/mm
Dielectric constant	1MHz	IEC 60250	2.85
Dielectric strength		IEC 60243-1	30	KV/mm
Dielectric constant	1 MHz	IEC 60250	2.85
Compared to the anti leakage trace index		UL 746	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ISO 2039-2	120
	Rockwell hardness	M-Sale	ISO 2039-2	50
		Rockwell hardness	M -Sale	ISO 2039-2	50
		Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	120
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut			>PC<

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 5330 /MT
Shenzhen Jiuhe	US$ 6620 /MT
Dongguan Jinghong Plastic	US$ 6680 /MT

Supplier Join

Get App

Top

PC TARFLON™ AZ1900T IDEMITSU JAPAN

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index