PC IDEMITSU JAPAN AZ1900T
High liquidity level
UL
US$ 6,489 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
bending strengthISO 17890.0 Mpa
Elongation at BreakISO 527-270 %
Charpy Notched Impact StrengthISO 17965 kJ/m²
Nominal tensile fracture strainISO 527-295 %
Impact strength of cantilever beam gapASTM D256/ISO 17980 kg·cm/cm(J/M)ft·lb/in
Rockwell hardnessASTM D785-
Bending modulusISO 1782300 Mpa
ASTM D790/ISO 1782400 kg/cm²(MPa)[Lb/in²]
elongationASTM D638/ISO 52764 %
Tensile modulusASTM D638/ISO 5272300 kg/cm²(MPa)[Lb/in²]
Elongation at BreakASTM D638/ISO 52792 %
tensile strengthYieldISO 527-265.0 Mpa
ASTM D638/ISO 52768 kg/cm²(MPa)[Lb/in²]
Physical propertiesTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
Shrinkage rate横向Flow : 2.00 mmInternal Method0.50 - 0.70 %
MD: 2.00 mmInternal Method0.5-0.7 %
TD:2.00mmInternal Method0.50-0.70 %
ASTM D9550.5-0.7 %
melt mass-flow rateASTM D1238/ISO 1133- g/10min
Water absorption rateEquilibrium, 23℃, 50% RHISO 620.23 %
Shrinkage rateMD:2.00mmInternal Method0.50-0.70 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113318.0 cm3/10min
densityASTM D792/ISO 11831.20
Water absorption rateASTM D570/ISO 62- %
Equilibrium, 23°C, 50% RHISO 620.23 %
Spiral flow lengthInternal Method29.0 CM
Melt Volume Flow Rate (MVR)MVRISO 11335 cm3/10min
Water absorption rateEquilibrium,23°C,50%RHISO 620.23 %
Shrinkage rateFlow : 2.00 mmInternal Method0.50 - 0.70 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11335.00 cm3/10min
Shrinkage rateTDInternal Method0.5-0.7 %
otherTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
characteristic高流动型
thermal performanceTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/A125 °C
Linear coefficient of thermal expansionASTM D696/ISO 11359- mm/mm.℃
UL flame retardant rating4.00 mmUL 945VA
RTI StrUL 74680.0 °C
Vicat softening temperatureASTM D1525/ISO R306- ℃（℉）
UL flame retardant rating1.50 mmUL 94V-0
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A125 °C
HDTASTM D648/ISO 75131 ℃（℉）
Linear coefficient of thermal expansionASTM D6960.000065 cm/cm/℃
RTI ElecUL 74680.0 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
FlowISO 11359-26.5E-5 cm/cm/°C
RTI ImpUL 74680.0 °C
RTIUL 74680.0 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B140 °C
Combustibility (rate)UL 94V-0/1.5mm
injectionTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
Temperature at the front of the material cylinder260 to 300 °C
Mold temperature80 to 120 °C
drying temperature120 °C
Temperature in the middle of the barrel260 to 300 °C
drying time5.0 to 8.0 hr
Temperature at the rear of the barrel260 to 300 °C
Electrical performanceTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
Compared to the anti leakage trace indexUL 746PLC 2
Dielectric strengthIEC 60243-130 KV/mm
Dielectric constant1MHzIEC 602502.85
Volume resistivityASTM D257/IEC 60093- Ω.cm
Dielectric constant1 MHzIEC 602502.85
hardnessTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
Rockwell hardnessM-SaleISO 2039-250
M -SaleISO 2039-250
R -SaleISO 2039-2120
R-SaleISO 2039-2120
flammabilityTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
UL flame retardant rating1.5mmUL 94V-0
ISO>PC<
UL flame retardant rating1.5 mmUL 94V-0
Supplementary InformationTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
ISO Shortcut>PC<
optical performanceTest ConditionTest MethodIDEMITSU JAPAN/AZ1900T
transmissivityISO 13468-185.0to89.0 %