PA6 Amilan® CM1016G-30 TORAY JAPAN

414

Unit Price:US$ 26,914 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-40°C	kJ/m²	70
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	kJ/m²	80

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.79mm		HB --

mechanical properties	Test Condition	Test Method	Test Result
bending strength	80°C	MPa	155 105
	bending strength	23°C	MPa	280 145
	bending strength	bending strength	-40°C	MPa	325 315
Bending modulus	80°C	MPa	4700 3500
	Bending modulus	23°C	MPa	9500 5100
	Bending modulus	Bending modulus	-40°C	MPa	11800 9800
Tensile strain	Break,80°C	%	4.0
	Tensile strain	Break,23°C	%	3.0 4.0
	Tensile strain	Tensile strain	Break,-40°C	%	3.0 3.0
tensile strength	80°C	MPa	100 70.0
Rockwell hardness		ASTM D785	R120.M93
tensile strength	-40°C	MPa	250 225
tensile strength	tensile strength	23°C	MPa	185 105
Compressive stress	-40°C	MPa	250 210
	Compressive stress	23°C		180 MPa
	Compressive stress	Compressive stress	80°C	MPa	95.0 70.0
shear strength	23°C	MPa	85.0 --
Taber abraser	1000Cycles	mg	0.350 --
Friction coefficient vs. Metal			0.15 --

thermal performance	Test Condition	Test Method	Test Result
Melting temperature			225 ℃（℉）
Hot deformation temperature	0.45MPa,Unannealed	°C	224 --
Melting temperature		°C	225 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	2.0E-5到3.0E-5 --
specific heat		J/kg/°C	1600 --
thermal conductivity		W/m/K	0.38 --

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	%	6.4 --
Water absorption rate	Water absorption rate	23°C,24hr	%	1.1 --
Shrinkage rate	MD:3.00mm4	%	0.20-0.40 --
Shrinkage rate	Shrinkage rate	TD:3.00mm3	%	0.50-0.80 --
Water absorption rate		ASTM D570/ISO 62	1.1 %
density		ASTM D792/ISO 1183	1.36

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		sec	131
Dissipation factor	23°C,1MHz		0.030 0.070
	Dissipation factor	23°C,1kHz		0.030 0.18
	Dissipation factor	Dissipation factor	23°C,50Hz		0.030 0.17
Volume resistivity		ASTM D257/IEC 60093	10^13 Ω.cm
Volume resistivity	Volume resistivity		ohms·cm	1E+15 1E+12
Dielectric strength		kV/mm	20 18
Dielectric constant	23°C,50Hz		4.90 10.7
	Dielectric constant	23°C,1kHz		4.60 7.90
	Dielectric constant	Dielectric constant	23°C,1MHz		4.00 4.30

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale,23°C		93 --
	Rockwell hardness	R-Sale,80°C		12 --
	Rockwell hardness	Rockwell hardness	R-Sale,23°C		120 --

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Amilan® CM1016G-30 TORAY JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet