Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1016G-30 TORAY JAPAN
Amilan®
Automotive sector
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM1016G-30 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 70 |
| 23°C | kJ/m² | 80 |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM1016G-30 |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | 93 -- | |
| R计秤,23°C | 120 -- | ||
| R计秤,80°C | 12 -- |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM1016G-30 |
|---|---|---|---|
| bending strength | -40°C | MPa | 325 315 |
| Taber abraser | 1000Cycles | mg | 0.350 -- |
| Flexural modulus | 23°C | MPa | 9500 5100 |
| bending strength | 23°C | MPa | 280 145 |
| tensile strength | 23°C | MPa | 185 105 |
| shear strength | 23°C | MPa | 85.0 -- |
| Flexural modulus | -40°C | MPa | 11800 9800 |
| Rockwell hardness | ASTM D785 | R120.M93 | |
| Tensile strain | 断裂,23°C | % | 3.0 4.0 |
| tensile strength | 80°C | MPa | 100 70.0 |
| bending strength | 80°C | MPa | 155 105 |
| compression stress | 23°C | 180 MPa | |
| 80°C | MPa | 95.0 70.0 | |
| Tensile strain | 断裂,80°C | % | 4.0 |
| 断裂,-40°C | % | 3.0 3.0 | |
| Flexural modulus | 80°C | MPa | 4700 3500 |
| tensile strength | -40°C | MPa | 250 225 |
| compression stress | -40°C | MPa | 250 210 |
| Friction coefficient - vs. Metal | 0.15 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM1016G-30 |
|---|---|---|---|
| Dissipation Factor | 23°C,1kHz | 0.030 0.18 | |
| arc resistance | sec | 131 | |
| dielectric constant | 23°C,50Hz | 4.90 10.7 | |
| Dissipation Factor | 23°C,1MHz | 0.030 0.070 | |
| dielectric strength | kV/mm | 20 18 | |
| Volume resistivity | ohms·cm | 1E+15 1E+12 | |
| dielectric constant | 23°C,1MHz | 4.00 4.30 | |
| Volume resistivity | ASTM D257/IEC 60093 | 10^13 Ω.cm | |
| Dissipation Factor | 23°C,50Hz | 0.030 0.17 | |
| dielectric constant | 23°C,1kHz | 4.60 7.90 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM1016G-30 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.36 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.1 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM1016G-30 |
|---|---|---|---|
| UL flame retardant rating | 0.79mm | HB -- |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM1016G-30 |
|---|---|---|---|
| Shrinkage rate | MD:3.00mm4 | % | 0.20-0.40 -- |
| Water absorption rate | 饱和,23°C | % | 6.4 -- |
| Shrinkage rate | TD:3.00mm3 | % | 0.50-0.80 -- |
| Water absorption rate | 23°C,24hr | % | 1.1 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM1016G-30 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 224 -- |
| melting temperature | °C | 225 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 2.0E-5到3.0E-5 -- |
| specific heat | J/kg/°C | 1600 -- | |
| thermal conductivity | W/m/K | 0.38 -- | |
| melting temperature | 225 ℃（℉） |