PA6

PA6 Zytel® 73G30HSL BK416 DUPONT USA

336

Unit Price:US$ 2,916 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Electronic and electrical components｜Automotive Applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	16 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	80 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	15 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	3.50 J

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	ISO 3795	50 mm/min
Atomization	F-value(refraction)	ISO 6452	95 %
Atomization	Atomization	G-value(condensate)	ISO 6452	1E-04 g
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	21 %
FMVSS flammability		FMVSS302	B

mechanical properties	Test Condition	Test Method	Test Result
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Bending modulus		ISO 178	8500 Mpa
bending strength		ISO 178	280 Mpa
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile strain	Break	ISO 527-2	3.5 %
tensile strength	Break	ISO 527-2	190 Mpa
Tensile modulus		ISO 527-2	9500 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	210 °C
Glass transition temperature		ISO 11357-2	60.0 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C
Vicat softening temperature		ISO 306/B50	215 °C
Melting temperature		ISO 11357-3	221 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7.5E-05 cm/cm/°C
Effective thermal diffusivity coefficient			9.1E-08 m²/s

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ISO 294-4	0.20 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.60 %
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	15.0 cm3/10min
density		ISO 1183	1.36 g/cm³
ThermalConductivityofMelt			0.26 W/m/K
SpecificHeatCapacity of Melt			2280 J/kg/°C
MediumDensity			1.20 g/cm³
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.9 %
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	6.3 %

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H961/30	ISO 2039-1	230 Mpa
Rockwell hardness	R-Scale	ISO 2039-2	121

Supplementary Information	Test Condition	Test Method	Test Result
Odor		VDA270	3.50
EmissionofOrganicCompounds		VDA277	8.50 µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Zytel® 73G30HSL BK416 DUPONT USA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet