Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73G30HSL BK416 DUPONT USA
Zytel®
Electronic and electrical、Automotive Applications
Thermal stability、Filler: Glass fiber reinf、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/73G30HSL BK416 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 16 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 80 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 3.50 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 15 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/73G30HSL BK416 |
|---|---|---|---|
| Odor | VDA270 | 3.50 | |
| Emissions of Organic Compounds | VDA277 | 8.50 µgC/g |
| hardness | Test Condition | Test Method | DUPONT USA/73G30HSL BK416 |
|---|---|---|---|
| ball-indentation hardness | H961/30 | ISO 2039-1 | 230 Mpa |
| Rockwell hardness | R级 | ISO 2039-2 | 121 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73G30HSL BK416 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9500 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| bending strength | ISO 178 | 280 Mpa | |
| Flexural modulus | ISO 178 | 8500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| tensile strength | 断裂 | ISO 527-2 | 190 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/73G30HSL BK416 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO 6452 | 95 % |
| G-value(condensate) | ISO 6452 | 1E-04 g | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| burning rate | 1.00mm | ISO 3795 | 50 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/73G30HSL BK416 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.3 % |
| MediumDensity | 1.20 g/cm³ | ||
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 15.0 cm3/10min |
| density | ISO 1183 | 1.36 g/cm³ | |
| SpecificHeatCapacity of Melt | 2280 J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.9 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73G30HSL BK416 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 221 °C | |
| Effective thermal diffusivity coefficient | 9.1E-08 m²/s | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| vicat | ISO 306/B50 | 215 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 210 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C |