Material Properties:Antichemical｜Hydrolysis resistance｜Fatigue resistance｜Thermal stability｜Glass fiber reinforced｜Lubricity｜Rigidity at high temperatures｜tensile strength ｜Heat resistance
Application Areas:Automotive sector｜Especially under high temperature conditions｜Designed to achieve greater structural strength｜Rigidity and hydrolysis resistance
Color:--
Grade:Heat resistant grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Water absorption rate		ISO 62	0.85 %
Water absorption rate	Water absorption rate		ISO 62	2.0 %
density		ISO 1183	1.32 g/cm³
Shrinkage rate		ISO 294-4	0.4 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.9 %

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ISO 527	174 Mpa
elongation		ISO 527	3 %
Tensile modulus		ISO 527	7500 Mpa
Flexural modulus		ISO 178	7700 Mpa
bending strength		ISO 178	250 Mpa
Impact strength of simply supported beam without notch		ISO 179	10.9 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179	9.8 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
dielectric strength		IEC 60243	16 KV/mm
Volume resistivity		IEC 60093	3 ohm-cm×1015

Thermal performance	Test Condition	Test Method	Test Result
melting temperature		ISO 3146	260 °C
Heat distortion temperature		ISO 75	250 °C
Heat distortion temperature	Heat distortion temperature		ISO 75	258 °C
UL flame retardant rating		UL 94	--

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.