Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 R525H ASCEND USA
Vydyne®
Automotive sector,Especially under high temperature conditions,Designed to achieve greater structural strength,Rigidity and hydrolysis resistance
Antichemical,Hydrolysis resistance,Fatigue resistance,Thermal stability,Glass fiber reinforced,Lubricity,Rigidity at high temperat,tensile strength ,Heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | ASCEND USA/R525H |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527 | 174 Mpa |
| bending strength | ISO 178 | 250 Mpa | |
| Flexural modulus | ISO 178 | 7700 Mpa | |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179 | 10.9 kJ/m² |
| elongation | 断裂 | ISO 527 | 3 % |
| Impact strength of simply supported beam without notch | -30℃ | ISO 179 | 9.8 kJ/m² |
| Tensile modulus | ISO 527 | 7500 Mpa |
| Electrical performance | Test Condition | Test Method | ASCEND USA/R525H |
|---|---|---|---|
| dielectric strength | IEC 60243 | 16 KV/mm | |
| Volume resistivity | IEC 60093 | 3 ohm-cm×1015 |
| physical property | Test Condition | Test Method | ASCEND USA/R525H |
|---|---|---|---|
| Shrinkage rate | 2mm,平行 | ISO 294-4 | 0.4 % |
| Water absorption rate | 23℃,24hrs | ISO 62 | 0.85 % |
| density | ISO 1183 | 1.32 g/cm³ | |
| Shrinkage rate | 2mm,垂直 | ISO 294-4 | 0.9 % |
| Water absorption rate | 23℃,50%湿度 | ISO 62 | 2.0 % |
| Thermal performance | Test Condition | Test Method | ASCEND USA/R525H |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，HDT | ISO 75 | 258 °C |
| melting temperature | ISO 3146 | 260 °C | |
| Heat distortion temperature | 1.82MPa，HDT | ISO 75 | 250 °C |
| UL flame retardant rating | UL 94 | -- |