PC Makrolon® 2400 COVESTRO GERMANY

260

Unit Price:US$ 3,542 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low viscosity
Application Areas:Automotive Applications｜Electrical applications｜Industrial applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
remarks			颗粒料注塑成型
characteristic			汽车领域的应用

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO 180/1A	75 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	12 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	NB NB
Charpy Notched Impact Strength		ISO 179/1eA	6.5
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	1.4

mechanical properties	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	113 Mpa
tensile strength	Break50 mm/min	ISO 527-1	70 Mpa
tensile strength	tensile strength	Yield50 mm/min	ISO 527-1	65 Mpa
elongation	Break50 mm/min	ISO 527-1	>= 50 %
	elongation	50 mm/min	ISO 527-1	120 %
	elongation	elongation	Yield50 mm/min	ISO 527-1	6.3 %
Tensile modulus	1 mm/min	ISO 527-1	2.35 GPa
bending strength	2 mm/min	ISO 178	96 Mpa
bending strength	bending strength	2 mm/min	ISO 178	72 Mpa
Bending modulus	2 mm/min	ISO 178	2.35 GPa
Tensile creep modulus	1 hr	ISO 899-1	2200 Mpa
Tensile creep modulus	Tensile creep modulus	1000 hr	ISO 899-1	1900 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Flow	ISO 11359-1	65 µm/m-°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-1	65 µm/m-°C
thermal conductivity		ISO 8302	0.2 W/m/K
Hot deformation temperature	0.46 MPa	ISO 75-1	139 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa	ISO 75-1	127 °C
Vicat softening temperature		ISO 306	147 °C
Vicat softening temperature	Vicat softening temperature		ISO 306	148 °C
Glass transition temperature, Tg	10°C/min	ISO 11357-1	147 °C
flammability		UL 94	HB
flammability	flammability		UL 94	V-2
Extreme Oxygen Index		ISO 4589-2	27 %

Physical properties	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.66 g/cc
density		ISO 1183-1	1.2 g/cc
Water absorption rate		ISO 62	0.12 %
Water absorption rate	Water absorption rate		ISO 62	0.3 %
Water vapor permeability		ISO 15106-1	15 g/m2
Shrinkage rate	Flow	ISO 294-4	0.0065 cm/cm
transverse		ISO 294-4	0.0065 cm/cm

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	10000000000000000 ohm·cm
Surface resistivity		IEC 60093	10000000000000000 Ohm
Dielectric constant		IEC 60250	3.1
Dielectric constant	Dielectric constant		IEC 60250	3
Dielectric strength		IEC 60243-1	34 KV/mm
Dissipation factor		IEC 60250	0.009
Dissipation factor	Dissipation factor		IEC 60250	0.00050
Compared to the anti leakage trace index		IEC 60112
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112

flame retardant performance	Test Condition	Test Method	Test Result
Glow wire combustion index (GWFI)		IEC 60695-2-12	850 °C
Glow wire combustion index (GWFI)	Glow wire combustion index (GWFI)		IEC 60695-2-13	875 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® 2400 COVESTRO GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet