Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 2400 COVESTRO GERMANY
Makrolon®
Automotive Applications、Electrical applications、Industrial applications
Low viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO GERMANY/2400 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 1.4 | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | NB NB | |
| Impact strength of cantilever beam gap | ISO 180/1A | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | COVESTRO GERMANY/2400 |
|---|---|---|---|
| tensile strength | 断裂50 mm/min | ISO 527-1 | 70 Mpa |
| Tensile creep modulus | 1000 hr | ISO 899-1 | 1900 Mpa |
| bending strength | 2 mm/min | ISO 178 | 72 Mpa |
| elongation | 50 mm/min | ISO 527-1 | 120 % |
| 屈服50 mm/min | ISO 527-1 | 6.3 % | |
| Tensile modulus | 1 mm/min | ISO 527-1 | 2.35 GPa |
| ball-indentation hardness | ISO 2039-1 | 113 Mpa | |
| tensile strength | 屈服50 mm/min | ISO 527-1 | 65 Mpa |
| elongation | 断裂50 mm/min | ISO 527-1 | >= 50 % |
| Flexural modulus | 2 mm/min | ISO 178 | 2.35 GPa |
| Tensile creep modulus | 1 hr | ISO 899-1 | 2200 Mpa |
| Electrical performance | Test Condition | Test Method | COVESTRO GERMANY/2400 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | ||
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| dielectric constant | IEC 60250 | 3 | |
| Volume resistivity | IEC 60093 | 10000000000000000 ohm·cm | |
| Dissipation Factor | IEC 60250 | 0.00050 | |
| Surface Resistivity | IEC 60093 | 10000000000000000 Ohm |
| other | Test Condition | Test Method | COVESTRO GERMANY/2400 |
|---|---|---|---|
| characteristic | 汽车领域的应用 | ||
| notes | 颗粒料 注塑成型 |
| Flame retardant performance | Test Condition | Test Method | COVESTRO GERMANY/2400 |
|---|---|---|---|
| Glow wire combustion index (GWFI) | IEC 60695-2-13 | 875 °C | |
| IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | COVESTRO GERMANY/2400 |
|---|---|---|---|
| Apparent density | ISO 60 | 0.66 g/cc | |
| Water absorption rate | ISO 62 | 0.3 % | |
| density | ISO 1183-1 | 1.2 g/cc | |
| Water Vapor Transmission Rate | ISO 15106-1 | 15 g/m2 | |
| horizontal | ISO 294-4 | 0.0065 cm/cm | |
| Shrinkage rate | Flow | ISO 294-4 | 0.0065 cm/cm |
| Thermal performance | Test Condition | Test Method | COVESTRO GERMANY/2400 |
|---|---|---|---|
| thermal conductivity | ISO 8302 | 0.2 W/m/K | |
| Heat distortion temperature | 0.46 MPa，HDT | ISO 75-1 | 139 °C |
| vicat | ISO 306 | 147 °C | |
| Glass transition temperature, Tg | 10°C/min | ISO 11357-1 | 147 °C |
| vicat | ISO 306 | 148 °C | |
| flammability | UL 94 | V-2 | |
| Heat distortion temperature | 1.8 MPa，HDT | ISO 75-1 | 127 °C |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-1 | 65 µm/m-°C |
| 横向 | ISO 11359-1 | 65 µm/m-°C |