ABS CYCOLAC™ FR15U BK4051 SABIC INNOVATIVE US
234
- Unit Price:US$ 3,779 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance｜Flame retardant
- Application Areas:small home appliances｜Automotive Applications｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 86.0 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 75.0 °C | |
| vicat | -- | ASTM D15258 | 93.0 °C |
| -- | ISO 306/B50 | 92.0 °C | |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 9.0E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 9.2E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 90.0 °C | |
| RTI Imp | UL 746 | 85.0 °C | |
| RTI | UL 746 | 90.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| 2.8 mm | UL 94 | 5VA |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 28.0 J |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 200°C, 1000 sec^-1 | ASTM D3835 | 320 Pa·s |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 230°C/3.8 kg | ASTM D1238 | 3.3 g/10 min |
| 220°C/5.0 kg | ISO 1133 | 7.0 g/10 min | |
| Melt volume flow rate | 220°C/10.0 kg | ISO 1133 | 40.0 cm3/10min |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | > 1.0E+14 ohms·cm | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 20 KV/mm |
| arc resistance | ASTM D495 | PLC 7 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| High arc combustion index (HAI) | UL 746 | PLC 4 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 90 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.10 % | ||
| Suggested injection volume | 50 to 70 % | ||
| Temperature at the rear of the barrel | 170 to 180 °C | ||
| Temperature in the middle of the barrel | 200 to 210 °C | ||
| Temperature at the front of the material cylinder | 205 to 220 °C | ||
| Spray nozzle temperature | 205 to 230 °C | ||
| Processing (melt) temperature | 205 to 230 °C | ||
| mold temperature | 50 to 70 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 30 to 60 rpm | ||
| Exhaust hole depth | 0.038 to 0.051 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2060 Mpa |
| -- | ISO 527-2/1 | 2210 Mpa | |
| tensile strength | 屈服3 | ASTM D638 | 37.0 Mpa |
| 屈服 | ISO 527-2/50 | 41.0 Mpa | |
| 断裂3 | ASTM D638 | 30.0 Mpa | |
| elongation | 屈服3 | ASTM D638 | 2.4 % |
| 断裂3 | ASTM D638 | 17 % | |
| 断裂 | ISO 527-2/50 | 22 % | |
| flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2340 Mpa |
| --5 | ISO 178 | 2260 Mpa | |
| bending strength | --5,6 | ISO 178 | 63.0 Mpa |
| 屈服, 50.0 mm 跨距4 | ASTM D790 | 67.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.