ABS FR15U BK4051 SABIC INNOVATIVE US

CYCOLAC™

small home appliances,Automotive Applications,Electrical applications

UV resistance,Flame retardant

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/FR15U BK4051
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	86.0 °C
Hot deformation temperature		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	75.0 °C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	9.2E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow : -40 to 40°C	ASTM E831	9.0E-5 cm/cm/°C
RTI		UL 746	90.0 °C
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	85.0 °C
Vicat softening temperature	--	ASTM D15258	93.0 °C
Vicat softening temperature		--	ISO 306/B50	92.0 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/FR15U BK4051
Bending modulus	50.0 mm Span4	ASTM D790	2340 Mpa
Bending modulus		--5	ISO 178	2260 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	67.0 Mpa
bending strength		--5,6	ISO 178	63.0 Mpa
elongation	Yield3	ASTM D638	2.4 %
		Break3	ASTM D638	17 %
		Break	ISO 527-2/50	22 %
Tensile modulus	--2	ASTM D638	2060 Mpa
Tensile modulus		--	ISO 527-2/1	2210 Mpa
tensile strength	Break3	ASTM D638	30.0 Mpa
		Yield	ISO 527-2/50	41.0 Mpa
		Yield3	ASTM D638	37.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/FR15U BK4051
Arc resistance		ASTM D495	PLC 7
Compared to the anti leakage trace index		UL 746	PLC 1
Dielectric strength	3.20 mm, in Oil	IEC 60243-1	20 KV/mm
High arc combustion index		UL 746	PLC 4
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 2
Volume resistivity		IEC 60093	> 1.0E+14 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/FR15U BK4051
melt mass-flow rate	230°C/3.8 kg	ASTM D1238	3.3 g/10 min
melt mass-flow rate		220°C/5.0 kg	ISO 1133	7.0 g/10 min
Melt Volume Flow Rate (MVR)	220°C/10.0 kg	ISO 1133	40.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/FR15U BK4051
Dart impact	23°C, Total Energy	ASTM D3763	28.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/FR15U BK4051
UL flame retardant rating	2.8 mm	UL 94	5VA
UL flame retardant rating		1.5 mm	UL 94	V-0

Filling analysis	Test Condition	Test Method	SABIC INNOVATIVE US/FR15U BK4051
Melt viscosity	200°C, 1000 sec^-1	ASTM D3835	320 Pa·s

injection	Test Condition	Test Method	SABIC INNOVATIVE US/FR15U BK4051
Back pressure			0.300 to 0.700 Mpa
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Exhaust hole depth			0.038 to 0.051 mm
Mold temperature			50 to 70 °C
Processing (melt) temperature			205 to 230 °C
Screw speed			30 to 60 rpm
Spray nozzle temperature			205 to 230 °C
Suggested injection volume			50 to 70 %
Suggested maximum moisture content			0.10 %
Temperature at the front of the material cylinder			205 to 220 °C
Temperature at the rear of the barrel			170 to 180 °C
Temperature in the middle of the barrel			200 to 210 °C