PC PANLITE® LN-1010RM TEIJIN JAPAN
203
- Unit Price:US$ 3,736 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50.1MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:LCD｜application
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D1525/ISO R306 | 139 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 137 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 125 °C | |
| vicat | ISO 306/B50 | 139 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C | |
| RTI Elec | 1.5mm | UL 746 | 80.0 °C |
| RTI Imp | 1.5mm | UL 746 | 80.0 °C |
| RTI Str | 1.5mm | UL 746 | 80.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 3.4 | |
| Dielectric loss | ASTM D150/IEC 60250 | 27 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.40 |
| 1MHz | IEC 60250 | 3.40 | |
| Dissipation Factor | 100Hz | IEC 60250 | 2.7E-03 |
| 1MHz | IEC 60250 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1330 | |
| shrinkage rate | ASTM D955 | 0.4-0.6 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % | |
| shrinkage rate | TD:4.00mm | 内部方法 | 0.40-0.60 % |
| MD:4.00mm | 内部方法 | 0.40-0.60 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638/ISO 527 | 2500 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 50 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 91 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 110 % | |
| Tensile modulus | ISO 527-2/1 | 2500 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 54.0 Mpa |
| 断裂 | ISO 527-2/50 | 50.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| 断裂 | ISO 527-2/50 | 110 % | |
| flexural modulus | ISO 178 | 2300 Mpa | |
| bending strength | ISO 178 | 91.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.