Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LN-1010RM TEIJIN JAPAN
PANLITE®
LCD,application
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/LN-1010RM |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/LN-1010RM |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric constant | ASTM D150/IEC 60250 | 3.4 | |
| relative permittivity | 100Hz | IEC 60250 | 3.40 |
| Dissipation Factor | 100Hz | IEC 60250 | 2.7E-03 |
| Dielectric loss | ASTM D150/IEC 60250 | 27 | |
| relative permittivity | 1MHz | IEC 60250 | 3.40 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/LN-1010RM |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 91 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2/1 | 2500 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 54.0 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 91.0 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 2500 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 110 % | |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| tensile strength | ASTM D638/ISO 527 | 50 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/LN-1010RM |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.4-0.6 % | |
| density | ASTM D792/ISO 1183 | 1330 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| flammability | Test Condition | Test Method | TEIJIN JAPAN/LN-1010RM |
|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/LN-1010RM |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.40-0.60 % |
| TD:4.00mm | 内部方法 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/LN-1010RM |
|---|---|---|---|
| vicat | ASTM D1525/ISO R306 | 139 ℃（℉） | |
| RTI Imp | 1.5mm | UL 746 | 80.0 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 137 °C |
| vicat | ISO 306/B50 | 139 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 125 °C |
| RTI Str | 1.5mm | UL 746 | 80.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI Elec | 1.5mm | UL 746 | 80.0 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |