PEI ULTEM™ ATX3562R-7301 SABIC INNOVATIVE US

376

Unit Price:US$ 10,460 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
13.5MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜High temperature resistance
Application Areas:Electronic and electrical components｜Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	5.4	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.6	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.8	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	5.6	kJ/m²
Impact strength of cantilever beam gap	3.20mm	ASTM D256	110	J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	12.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield,50.0mmSpan	ASTM D790	180	Mpa
bending strength	bending strength		ISO 178	172	Mpa
Bending modulus		ISO 178	13600	Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	12900	Mpa
Tensile strain	Break	ISO 527-2/5	1.4	%
elongation	Break	ASTM D638	2.5	%
Tensile strain	Yield	ISO 527-2/5	1.4	%
elongation	Yield	ASTM D638	2.5	%
tensile strength	Break	ISO 527-2/5	121	Mpa
	tensile strength	Break	ASTM D638	125	Mpa
		tensile strength	Yield	ISO 527-2/5	121	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	125	Mpa
Tensile modulus		ISO 527-2/1	14700	Mpa
Tensile modulus	Tensile modulus		ASTM D638	14900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to150°C	ISO 11359-2	3.8E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	195	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	183	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	182	°C
Vicat softening temperature		ASTM D152510	184	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	187	°C
Linear coefficient of thermal expansion	MD：23to150°C	ISO 11359-2	1.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to150°C	ASTME831	3.8E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	195	°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to150°C	ASTME831	1.6E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.040	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.10	%
Shrinkage rate	TD：3.20mm	Internal Method	0.30-0.50	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.30	%
Melt Volume Flow Rate (MVR)	360°C/5.0kg	ISO 1133	20.0	cm3/10min
melt mass-flow rate	337°C/6.6kg	ASTM D1238	20	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	6E+15	ohms·cm
Surface resistivity		ASTM D257	2.1E+15	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PEI ULTEM™ ATX3562R-7301 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index