Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI ATX3562R-7301 SABIC INNOVATIVE US
ULTEM™
Electronic and electrical、Automotive components
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/ATX3562R-7301 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.8 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 5.6 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 12.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.4 kJ/m² |
| 23°C | ISO 180/1A | 5.6 kJ/m² | |
| 3.20mm | ASTM D256 | 110 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/ATX3562R-7301 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 14700 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 121 Mpa |
| elongation | 屈服 | ASTM D638 | 2.5 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 1.4 % |
| tensile strength | 断裂 | ASTM D638 | 125 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 12900 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 121 Mpa |
| Tensile modulus | ASTM D638 | 14900 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.5 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 180 Mpa |
| ISO 178 | 172 Mpa | ||
| Flexural modulus | ISO 178 | 13600 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 1.4 % |
| tensile strength | 屈服 | ASTM D638 | 125 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/ATX3562R-7301 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 6E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | 2.1E+15 ohms |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/ATX3562R-7301 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.30 % |
| Melt volume flow rate | 360°C/5.0kg | ISO 1133 | 20.0 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.30-0.50 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.040 % |
| 饱和,23°C | ISO 62 | 0.10 % | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/ATX3562R-7301 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 195 °C |
| vicat | -- | ISO 306/B120 | 195 °C |
| Linear coefficient of thermal expansion | TD：23to150°C | ISO 11359-2 | 3.8E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 187 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 182 °C |
| vicat | ASTM D152510 | 184 °C | |
| Linear coefficient of thermal expansion | MD：-40to150°C | ASTME831 | 1.6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 183 °C |
| Linear coefficient of thermal expansion | TD：-40to150°C | ASTME831 | 3.8E-05 cm/cm/°C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：23到150°C | ISO 11359-2 | 1.6E-05 cm/cm/°C |