PBT

PBT Toraycon® 1101G-X54 TORAY JAPAN

310

Unit Price:US$ 3,390 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
73.1MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜Fast forming cycle｜Flame retardant｜Glass fiber reinforced
Application Areas:Electrical field｜Electronic field｜Automotive sector
Color:--
Grade:Enhanced level

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			玻璃纤维增强级.高抗冲击.耐热性

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	65 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	23℃·24hr	ASTM D-570	0.07 %

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	Notched，-40℃，1/8时宽	ASTM D-256	- kg·cm/cm
bending strength	23℃	ASTM D-790	1700 kg/cm
tensile strength	23℃	ASTM D-638	1200 kg/cm
Elongation at Break	23℃	ASTM D-638	5 %
Rockwell hardness	23℃	ASTM D-785	89 M标度
Bending modulus	23℃	ASTM D-790	72 kg/cm
Impact strength of cantilever beam gap	Unnotched，23℃，1/8时宽	ASTM D-256	60 kg·cm/cm
	Impact strength of cantilever beam gap	Unnotched，-40℃，1/8时宽	ASTM D-256	- kg·cm/cm
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Notched，23℃，1/8时宽	ASTM D-256	16 kg·cm/cm
tensile strength	23℃	ASTM D638	120 Mpa
elongation	23℃	ASTM D638	4 %
bending strength	23℃	ASTM D790	175 Mpa
Bending modulus	23℃	ASTM D790	7.6 GPa
Impact strength of cantilever beam gap	Notched，23℃	ASTM D256	185 J/m
	Impact strength of cantilever beam gap	Notched，-40℃	ASTM D256	135 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Unnotched，23℃	ASTM D256	60 KJ/m
Rockwell hardness		ASTM D785	90 M
Friction coefficient	对金属	ASTM D1894	0.17
Friction coefficient	Friction coefficient	对本身	ASTM D1894	0.20
tensile strength	Yield,23°C	ISO 527-2	120 Mpa
Bending modulus	23°C	ISO 178	8000 Mpa
Tensile modulus	23°C	ISO 527-2	8500 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.5 %
Friction coefficient vs. Metal		SuzukiMethod	0.17
Friction coefficient			0.20
bending strength	23°C	ISO 178	190 Mpa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	185 kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap		ASTM D256/ISO 179	135 kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	60 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	4 %
tensile strength		ASTM D638/ISO 527	120 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M90
Bending modulus		ASTM D790/ISO 178	7600 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	175 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ASTM D-696	2.5 cm/cm℃×10
Hot deformation temperature	0.45MPa	ASTM D648	220 °C
Hot deformation temperature	Hot deformation temperature	1.82Mpa	ASTM D648	210 °C
Linear coefficient of thermal expansion		ASTM D696	2.5
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	207 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C
Linear coefficient of thermal expansion	MD：-30to100°C	ISO 11359-2	4.2E-05 cm/cm/°C
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	210 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2.5x10^-5 mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	80×80×3板材		0.4-1.0 %
Hot deformation temperature	4.6kg/cm	ASTM D-648	220 °C
Hot deformation temperature	Hot deformation temperature	18.6kg.cm	ASTM D-648	210 °C
Water absorption rate	23℃,24hr	ASTM D570	0.07 %
Shrinkage rate	TD:3.00mm2	Internal Method	1.0 %
Water absorption rate	23°C,24hr	ISO 62	0.070 %
Shrinkage rate	MD:3.00mm4	Internal Method	0.40 %
density		ASTM D792/ISO 1183	1.46
Water absorption rate		ASTM D570/ISO 62	0.07 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D-257	7.5(2.2) cm×10
Arc resistance		ASTM D-495	131 秒
Dielectric strength	短时·23℃·1/8时	ASTM D-149	27(18) KV/mm
Arc resistance		ASTM D495	131 S
Volume resistivity		ASTM D257	7.0
Dielectric strength		ASTM D149	28 MV/m
Dielectric constant	50Hz	ASTM D150	3.8
Dielectric constant	Dielectric constant	10	ASTM D150	3.7
Dielectric loss	50Hz，Tangent	ASTM D150	0.002
Dielectric loss	Dielectric loss	10，Tangent	ASTM D150	0.02
Dielectric constant	23°C,50Hz	IEC 60250	3.80
Dielectric strength		IEC 60243-1	28 KV/mm
Dissipation factor	23°C,1MHz	IEC 60250	0.020
Arc resistance		IEC 60950	131 sec
Volume resistivity		IEC 60093	1.4E+17 ohms·cm
Dielectric constant	23°C,1kHz	IEC 60250	3.70
Dissipation factor	23°C,50Hz	IEC 60250	2E-03
Dielectric constant		ASTM D150/IEC 60250	3.8
Volume resistivity		ASTM D257/IEC 60093	7.0x10^14 Ω.cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale,23°C	ISO 2039-2	55

Supplementary Information	Test Condition	Test Method	Test Result
BarFlowLength	250°C,1.00mm	Internal Method	7.50 CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Toraycon® 1101G-X54 TORAY JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet