Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1101G-X54 TORAY JAPAN
Toraycon®
Electrical field、Electronic field、Automotive sector
High impact resistance、Fast forming cycle、Flame retardant、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 65 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 55 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 7.50 CM |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| Water absorption rate | 23℃·24小时 | ASTM D-570 | 0.07 % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 60 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 175 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 无缺口，-40℃，1/8时宽 | ASTM D-256 | - kg·cm/cm |
| Rockwell hardness | 23℃ | ASTM D-785 | 89 M标度 |
| Tensile modulus | 23°C | ISO 527-2 | 8500 Mpa |
| elongation at break | ASTM D638/ISO 527 | 4 % | |
| Rockwell hardness | ASTM D785 | M90 | |
| Impact strength of cantilever beam gap | 无缺口，23℃，1/8时宽 | ASTM D-256 | 60 kg·cm/cm |
| elongation | 23℃ | ASTM D638 | 4 % |
| Flexural modulus | 23°C | ISO 178 | 8000 Mpa |
| tensile strength | 23℃ | ASTM D638 | 120 Mpa |
| Impact strength of cantilever beam gap | 缺口，23℃ | ASTM D256 | 185 J/m |
| 缺口，-40℃ | ASTM D256 | 135 J/m | |
| coefficient of friction | 对金属 | ASTM D1894 | 0.17 |
| Impact strength of cantilever beam gap | 无缺口，23℃ | ASTM D256 | 60 KJ/m |
| Flexural modulus | ASTM D790/ISO 178 | 7600 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 90 M | |
| coefficient of friction | 0.20 | ||
| bending strength | 23℃ | ASTM D790 | 175 Mpa |
| Flexural modulus | 23℃ | ASTM D790 | 7.6 GPa |
| tensile strength | ASTM D638/ISO 527 | 120 kg/cm²(MPa)[Lb/in²] | |
| coefficient of friction | 对本身 | ASTM D1894 | 0.20 |
| Friction coefficient - vs. Metal | SuzukiMethod | 0.17 | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.5 % |
| Impact strength of cantilever beam gap | 缺口，23℃，1/8时宽 | ASTM D-256 | 16 kg·cm/cm |
| bending strength | 23°C | ISO 178 | 190 Mpa |
| Impact strength of cantilever beam gap | 缺口，-40℃，1/8时宽 | ASTM D-256 | - kg·cm/cm |
| bending strength | 23℃ | ASTM D-790 | 1700 kg/cm |
| elongation at break | 23℃ | ASTM D-638 | 5 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 120 Mpa |
| Flexural modulus | 23℃ | ASTM D-790 | 72 kg/cm |
| tensile strength | 23℃ | ASTM D-638 | 1200 kg/cm |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| arc resistance | ASTM D495 | 131 S | |
| dielectric constant | 50Hz | ASTM D150 | 3.8 |
| Dielectric loss | 10，正切 | ASTM D150 | 0.02 |
| dielectric strength | ASTM D149 | 28 MV/m | |
| dielectric constant | ASTM D150/IEC 60250 | 3.8 | |
| Dielectric loss | 50Hz，正切 | ASTM D150 | 0.002 |
| Volume resistivity | ASTM D-257 | 7.5(2.2) cm×10 | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| Volume resistivity | ASTM D257/IEC 60093 | 7.0x10^14 Ω.cm | |
| arc resistance | ASTM D-495 | 131 秒 | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 0.020 |
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.80 |
| 23°C,1kHz | IEC 60250 | 3.70 | |
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| arc resistance | IEC 60950 | 131 sec | |
| Volume resistivity | IEC 60093 | 1.4E+17 ohms·cm | |
| dielectric strength | 短时·23℃·1/8时 | ASTM D-149 | 27(18) KV/mm |
| dielectric constant | 10 | ASTM D150 | 3.7 |
| Volume resistivity | ASTM D257 | 7.0 |
| other | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| characteristic | 玻璃纤维增强级.高抗冲击.耐热性 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.46 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.0 % |
| MD:3.00mm4 | 内部方法 | 0.40 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| Heat distortion temperature | 4.6kg/cm | ASTM D-648 | 220 °C |
| Water absorption rate | 23℃,24hr | ASTM D570 | 0.07 % |
| Shrinkage rate | 80×80×3板材 | 0.4-1.0 % | |
| Heat distortion temperature | 18.6kg.cm | ASTM D-648 | 210 °C |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/1101G-X54 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 0.45MPa，HDT | ASTM D648 | 220 °C |
| HDT | ASTM D648/ISO 75 | 210 ℃（℉） | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 207 °C | |
| Linear coefficient of thermal expansion | ASTM D-696 | 2.5 cm/cm℃×10 | |
| MD：-30到100°C | ISO 11359-2 | 4.2E-05 cm/cm/°C | |
| Heat distortion temperature | 1.82Mpa，HDT | ASTM D648 | 210 °C |
| Linear coefficient of thermal expansion | ASTM D696 | 2.5 | |
| ASTM D696/ISO 11359 | 2.5x10^-5 mm/mm.℃ | ||
| UL flame retardant rating | UL 94 | HB |