PA12 LNP™ LUBRICOMP™ SCL36 SABIC INNOVATIVE US

340

Unit Price:US$ 9,520 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
44.8MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:lubrication｜wear resistant
Application Areas:Electrical appliances｜Plastic bag
Color:--
Grade:Conductive grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	--	ISO 6603-2	4.00	J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	14.0	J
Suspended wall beam without notch impact strength	23°C6	ISO 180/1U	39	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	690	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor		ASTM D3702	0.0 4.4E+6	10^-8 mm³/N·m
Friction coefficient	Static	ASTM D3702	0.30
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702	0.41
bending strength	Break, 50.0 mm Span3	ASTM D790	214	Mpa
	bending strength	Yield, 50.0 mm Span3	ASTM D790	215	Mpa
	bending strength	bending strength	--	ISO 178	206	Mpa
Bending modulus	--4	ISO 178	16500	Mpa
Bending modulus	Bending modulus	50.0 mm Span3	ASTM D790	15800	Mpa
elongation	Break	ISO 527-2/5	1.0	%
elongation	elongation	Break2	ASTM D638	1.9	%
tensile strength	Break	ISO 527-2/5	130	Mpa
tensile strength	tensile strength	Break2	ASTM D638	157	Mpa
Tensile modulus	--	ISO 527-2/1	19400	Mpa
Tensile modulus	Tensile modulus	--1	ASTM D638	21400	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
drying time			4.0	hr
Suggested maximum moisture content			0.12 to 0.20	%
Temperature at the rear of the barrel			215 to 225	°C
Temperature in the middle of the barrel			220 to 230	°C
Temperature at the front of the material cylinder			225 to 240	°C
Processing (melt) temperature			225 to 240	°C
Mold temperature			70 to 80	°C
Back pressure			0.200 to 0.300	Mpa
Screw speed			30 to 60	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	173	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span6	ISO 75-2/Af	170	°C
		Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span6	ISO 75-2/Bf	177	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	178	°C
Linear coefficient of thermal expansion	Flow : -30 to 30°C	ASTM D696	2.9E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -30 to 30°C	ASTM D696	6.3E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.14	%
Water absorption rate	Water absorption rate	24 hr, 50% RH	ASTM D570	0.090	%
Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	0.40 - 0.60	%
Shrinkage rate	Shrinkage rate	Flow : 24hr	ASTM D955	0.040 - 0.060	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA12 LNP™ LUBRICOMP™ SCL36 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index