Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 SCL36 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Plastic bag
lubrication、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 690 J/m |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 14.0 J |
| Suspended wall beam without notch impact strength | 23°C6 | ISO 180/1U | 39 kJ/m² |
| Dart impact | -- | ISO 6603-2 | 4.00 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Tensile modulus | --1 | ASTM D638 | 21400 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 130 Mpa |
| elongation | 断裂2 | ASTM D638 | 1.9 % |
| bending strength | -- | ISO 178 | 206 Mpa |
| Flexural modulus | --4 | ISO 178 | 16500 Mpa |
| bending strength | 屈服, 50.0 mm 跨距3 | ASTM D790 | 215 Mpa |
| Flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 15800 Mpa |
| coefficient of friction | Dynamic | ASTM D3702 | 0.41 |
| tensile strength | 断裂2 | ASTM D638 | 157 Mpa |
| coefficient of friction | Static | ASTM D3702 | 0.30 |
| Tensile modulus | -- | ISO 527-2/1 | 19400 Mpa |
| bending strength | 断裂, 50.0 mm 跨距3 | ASTM D790 | 214 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 1.0 % |
| Wear factor | ASTM D3702 | 0.0 4.4E+6 10^-8 mm³/N·m |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Shrinkage rate | 流动 : 24小时 | ASTM D955 | 0.040 - 0.060 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.14 % |
| 24 hr, 50% RH | ASTM D570 | 0.090 % | |
| Shrinkage rate | 横向流动 : 24小时 | ASTM D955 | 0.40 - 0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -30 到 30°C | ASTM D696 | 2.9E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 178 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距6，HDT | ISO 75-2/Af | 170 °C | |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距6，HDT | ISO 75-2/Bf | 177 °C | |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 173 °C | |
| Linear coefficient of thermal expansion | 横向 : -30 到 30°C | ASTM D696 | 6.3E-5 cm/cm/°C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/SCL36 |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.12 to 0.20 % | ||
| Temperature in the middle of the barrel | 220 to 230 °C | ||
| Temperature at the rear of the barrel | 215 to 225 °C | ||
| Processing (melt) temperature | 225 to 240 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 225 to 240 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| Temperature | 70 to 80 °C |