PA66 Durethan®  AKV30H1.0-NC LANXESS GERMANY

298
  • Unit Price:US$ 3,445 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    87MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Filler: Glass fiber reinforced material30%Filler by weight
  • Application Areas:--
  • Color:--
  • Grade:Enhanced level

Technical Data Sheet Compare

hardnessTest ConditionTest MethodTest Result
ball-indentation hardnessISO 2039-1230 Mpa
otherTest ConditionTest MethodTest Result
notes30%玻纤增强.热稳定级
thermal performanceTest ConditionTest MethodTest Result
Heat Deflection TemperatureHDTASTM D648/ISO 751.36 ℃(℉)
melting temperature263 ℃(℉)
vicatASTM D1525/ISO R306>230 ℃(℉)
vicatISO 306/B120>230 °C
melting temperatureISO 11357-3263 °C
Linear coefficient of thermal expansionMD:23到55°CISO 11359-22.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:23to55°CISO 11359-21E-04 cm/cm/°C
Heat Deflection Temperature0.45MPa,未退火ISO 75-2/B250 °C
Heat Deflection Temperature1.8MPa,未退火ISO 75-2/A250 °C
Heat Deflection Temperature8.0MPa,未退火ISO 75-2/C135 °C
processabilityTest ConditionTest MethodTest Result
mold temperature80 °C
Melt Temperature290 °C
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.6mmUL 94HB
UL flame retardant rating3.2mmUL 94HB
Burning wire flammability index2.0mmIEC 60695-2-12600 °C
Limiting Oxygen IndexISO 4589-223 %
Supplementary InformationTest ConditionTest MethodTest Result
ISO ShortcutISO 1874PA66.GR.14-110.GF30
Impact resistanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eU70 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU90 kJ/m²
Electrical performanceTest ConditionTest MethodTest Result
Surface ResistivityASTM D257/IEC 6009310 14(10 13) Ω
arc resistanceASTM D495/IEC 6011240(35)
volume resistivityASTM D257/IEC 6009310 13(10 11) Ω.cm
Surface ResistivityIEC 600931E+14 ohms
volume resistivity23°CIEC 600931E+15 ohms·cm
dielectric strength23°C,1.00mmIEC 60243-140 KV/mm
relative permittivity23°C,100HzIEC 602504.00
relative permittivity23°C,1MHzIEC 602504.00
Dissipation Factor23°C,100HzIEC 602509E-03
Dissipation Factor23°C,1MHzIEC 602500.018
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 0
Physical propertiesTest ConditionTest MethodTest Result
shrinkage rateASTM D9550.353) %
Apparent densityISO 600.70 g/cm³
shrinkage rateTD:280°C,3.00mm2ISO 25771.5 %
shrinkage rateTD:120°C,2hr,3.00mm3ISO 294-40.050 %
shrinkage rateMD:280°C,3.00mm2ISO 25770.35 %
shrinkage rateMD:120°C,2hr,3.00mm3ISO 25770.040 %
Water absorption rate饱和,23°CISO 625.5 %
Water absorption rate平衡,23°C,50%RHISO 622.0 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D638/ISO 52710600-7000 kg/cm²(MPa)[Lb/in²]
tensile strengthASTM D638/ISO 527185-120 kg/cm²(MPa)[Lb/in²]
flexural modulusASTM D790/ISO 1788400-5900 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 178290-200 kg·cm/cm(J/M)ft·lb/in
Elongation at breakASTM D638/ISO 5273.0-6.0 %
tensile strength断裂,23°CASTM D638179 Mpa
tensile strength断裂,23°CISO 527-2/5185 Mpa
elongation断裂,23°CASTM D6383.0 %
Tensile strain断裂,23°CISO 527-2/53.0 %
flexural modulus23°CASTM D790841 Mpa
flexural modulus23°CISO 178/A8400 Mpa
bending strength23°CASTM D790290 Mpa
bending strength3.5%StrainISO 178/A-- Mpa
bending strength23°CISO 178290 Mpa
bending strengthFlexuralStrainatFlexuralStrength5(23°C)4.0 %
Tensile modulus23°CASTM D63810300 Mpa
Tensile modulus23°CISO 527-2/110600 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.