PA66 AKV30H1.0-NC LANXESS GERMANY
Durethan® 
--
Filler: Glass fiber reinf,30%,Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
Impact strength of simply supported beam without notch23°CISO 179/1eU90 kJ/m²
-30°CISO 179/1eU70 kJ/m²
hardnessTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
ball-indentation hardnessISO 2039-1230 Mpa
Supplementary InformationTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
ISO ShortcutISO 1874PA66.GR.14-110.GF30
Electrical performanceTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
Surface ResistivityASTM D257/IEC 6009310 14(10 13) Ω
dielectric strength23°C,1.00mmIEC 60243-140 KV/mm
relative permittivity23°C,1MHzIEC 602504.00
Volume resistivity23°CIEC 600931E+15 ohms·cm
relative permittivity23°C,100HzIEC 602504.00
arc resistanceASTM D495/IEC 6011240(35)
Volume resistivityASTM D257/IEC 6009310 13(10 11) Ω.cm
Surface ResistivityIEC 600931E+14 ohms
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 0
Dissipation Factor23°C,100HzIEC 602509E-03
23°C,1MHzIEC 602500.018
Mechanical propertiesTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
Tensile strain断裂,23°CISO 527-2/53.0 %
Flexural modulus23°CISO 178/A8400 Mpa
bending strength3.5%StrainISO 178/A-- Mpa
tensile strength 断裂,23°CISO 527-2/5185 Mpa
bending strength23°CASTM D790290 Mpa
Tensile modulus23°CASTM D63810300 Mpa
23°CISO 527-2/110600 Mpa
Flexural modulusASTM D790/ISO 1788400-5900 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 178290-200 kg·cm/cm(J/M)ft·lb/in
elongation at breakASTM D638/ISO 5273.0-6.0 %
tensile strength 断裂,23°CASTM D638179 Mpa
ASTM D638/ISO 527185-120 kg/cm²(MPa)[Lb/in²]
bending strength23°CISO 178290 Mpa
Tensile modulusASTM D638/ISO 52710600-7000 kg/cm²(MPa)[Lb/in²]
Flexural modulus23°CASTM D790841 Mpa
elongation断裂,23°CASTM D6383.0 %
bending strengthFlexuralStrainatFlexuralStrength5(23°C)4.0 %
otherTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
notes30%玻纤增强.热稳定级
Physical propertiesTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
Shrinkage rateASTM D9550.353) %
processabilityTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
Melt Temperature290 °C
Temperature80 °C
flammabilityTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
UL flame retardant rating3.2mmUL 94HB
Burning wire flammability index2.0mmIEC 60695-2-12600 °C
Limiting Oxygen IndexISO 4589-223 %
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
Shrinkage rateMD:280°C,3.00mm2ISO 25770.35 %
Apparent densityISO 600.70 g/cm³
Water absorption rate平衡,23°C,50%RHISO 622.0 %
Shrinkage rateTD:280°C,3.00mm2ISO 25771.5 %
Water absorption rate饱和,23°CISO 625.5 %
Shrinkage rateMD:120°C,2hr,3.00mm3ISO 25770.040 %
TD:120°C,2hr,3.00mm3ISO 294-40.050 %
Thermal performanceTest ConditionTest MethodLANXESS GERMANY/AKV30H1.0-NC
melting temperatureISO 11357-3263 °C
Heat distortion temperatureHDTASTM D648/ISO 751.36 ℃（℉）
vicatASTM D1525/ISO R306>230 ℃（℉）
ISO 306/B120>230 °C
Linear coefficient of thermal expansionMD：23到55°CISO 11359-22.5E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B250 °C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-21E-04 cm/cm/°C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A250 °C
melting temperature263 ℃（℉）
Heat distortion temperature8.0MPa,未退火，HDTISO 75-2/C135 °C