PC/ABS

PC/ABS INFINO® HP-1000XA K21315 Samsung Cheil South Korea

238

Unit Price:US$ 2,667 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Easy to process｜High impact resistance｜heat-resisting｜Thermal stability｜High rigidity｜Dimensional stability｜Chemical resistance
Application Areas:Automotive sector｜Engineering accessories｜Application in the automotive field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	49 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	45 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	80.0 Mpa
Bending modulus		ASTM D790	2000 Mpa
Tensile strain	Break	ISO 527-2/50	100 %
elongation	Break	ASTM D638	100 %
tensile strength	Break	ISO 527-2/50	53.0 Mpa
	tensile strength	Break	ASTM D638	59.0 Mpa
		tensile strength	Yield	ISO 527-2/50	50.0 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	54.0 Mpa
Tensile modulus		ISO 527-2/50	2000 Mpa
Tensile modulus	Tensile modulus		ASTM D638	2000 Mpa
bending strength		ASTM D790	74.0 Mpa
Bending modulus		ISO 178	2100 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	110 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	125 °C
Vicat softening temperature	--	ISO 306/B120	125 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	123 °C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	112 °C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	102 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	123 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:3.20mm	ISO 2577	0.40-0.70 %
	Shrinkage rate	TD：3.20mm	ASTM D955	0.40-0.70 %
	Shrinkage rate	Shrinkage rate	MD：3.20mm	ASTM D955	0.40-0.70 %
melt mass-flow rate	250°C/10.0kg	ISO 1133	27 g/10min
melt mass-flow rate	melt mass-flow rate	250°C/10.0kg	ASTM D1238	27 g/10min
Shrinkage rate	MD:3.20mm	ISO 2577	0.40-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	113
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	113

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS INFINO® HP-1000XA K21315 Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet