Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS HP-1000XA K21315 Samsung Cheil South Korea
INFINO®
Automotive sector、Engineering accessories、Application in the automo
Easy to process、High impact resistance、heat-resisting、Thermal stability、High rigidity、Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/HP-1000XA K21315 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 49 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 45 kJ/m² |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/HP-1000XA K21315 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 113 |
| R级 | ASTM D785 | 113 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/HP-1000XA K21315 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2000 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 50.0 Mpa |
| elongation | 断裂 | ASTM D638 | 100 % |
| Tensile modulus | ISO 527-2/50 | 2000 Mpa | |
| bending strength | ISO 178 | 80.0 Mpa | |
| Flexural modulus | ISO 178 | 2100 Mpa | |
| bending strength | ASTM D790 | 74.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 59.0 Mpa |
| 屈服 | ASTM D638 | 54.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| Flexural modulus | ASTM D790 | 2000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 53.0 Mpa |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/HP-1000XA K21315 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40-0.70 % |
| TD:3.20mm | ISO 2577 | 0.40-0.70 % | |
| TD：3.20mm | ASTM D955 | 0.40-0.70 % | |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 27 g/10min |
| 250°C/10.0kg | ISO 1133 | 27 g/10min | |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.40-0.70 % |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/HP-1000XA K21315 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 102 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 110 °C | |
| vicat | -- | ISO 306/B120 | 125 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 123 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 112 °C | |
| vicat | -- | ISO 306/B50 | 123 °C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 125 °C |