POM

POM TENAC™-C HC460 ASAHI JAPAN

279

Unit Price:US$ 3,405 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance｜scratch resistance ｜wear resistant｜Medium viscosity
Application Areas:Engineering accessories｜Shell｜Automotive sector｜Engine parts｜Application in the automotive field｜currency
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			耐磨蚀性良好

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	7.0 kJ/m²
Tensile strain	Break,23℃	ISO 527-2	55 %
tensile strength	Yield, 23℃	ISO 527-2	69.0 Mpa
Tensile modulus	23℃	ISO 527-2	3000 Mpa
bending strength		ASTM D790	88.0 Mpa
Bending modulus		ASTMD790	2600 Mpa
elongation	Break	ASTMD638	40 %
tensile strength	--	ASTM D638	64.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2	66.0 Mpa
Tensile modulus		ISO 527-2	2750 Mpa
Tensile modulus	Tensile modulus		ASTM D638/ISO 527	3000(MPa) kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity			0.23 W/m/K
specific heat			1470 J/kg/°C
Linear coefficient of thermal expansion	MD	ASTMD696	1E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	102 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	124 °C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	158 °C
			Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	163 °C
				Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	158 °C
				Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	102 °C
UL flame retardant rating	0.750 mm	UL 94	HB
Combustibility (rate)		UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	Internal Method	1.6-2.0 %
melt mass-flow rate		ISO 1133	8.0 g/10 min
Water absorption rate	23°C,24hr,50%RH	ASTM D570	0.20 %
Shrinkage rate	MD	Internal Method	1.6-2.0 %
melt mass-flow rate	190°C/2.16kg	ISO 1133	8.0 g/10min
density		ASTM D792/ISO 1183	1.41
Shrinkage rate		ASTM D955	1.6-2.0 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	88
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	117

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top