Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM HC460 ASAHI JAPAN
TENAC™-C
Engineering accessories,Shell,Automotive sector,Engine parts,Application in the automotive field,currency
UV resistance,scratch resistance ,wear resistant,Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 88 |
| R级 | ASTM D785 | 117 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2750 Mpa | |
| elongation | 断裂 | ASTMD638 | 40 % |
| tensile strength | -- | ASTM D638 | 64.0 Mpa |
| Flexural modulus | ASTMD790 | 2600 Mpa | |
| Tensile strain | 断裂,23℃ | ISO 527-2 | 55 % |
| Charpy Notched Impact Strength | ISO 179 | 7.0 kJ/m² | |
| bending strength | ASTM D790 | 88.0 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 3000(MPa) kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 屈服 | ISO 527-2 | 66.0 Mpa |
| 屈服, 23℃ | ISO 527-2 | 69.0 Mpa | |
| Tensile modulus | 23℃ | ISO 527-2 | 3000 Mpa |
| other | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| characteristic | 耐磨蚀性良好 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.6-2.0 % | |
| density | ASTM D792/ISO 1183 | 1.41 |
| flammability | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.6-2.0 % |
| melt mass-flow rate | ISO 1133 | 8.0 g/10 min | |
| 190°C/2.16kg | ISO 1133 | 8.0 g/10min | |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 124 °C |
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 163 °C |
| 0.45 MPa, 未退火，HDT | ISO 75-2/B | 158 °C | |
| thermal conductivity | 0.23 W/m/K | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 158 °C |
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 102 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 102 °C | |
| specific heat | 1470 J/kg/°C | ||
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |