PA66 Leona™ 1402S ASAHI JAPAN

Unit Price:US$ 4,680 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Jiantou Plastic Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Thermal stability｜Fatigue resistance｜high strength｜High rigidity
Application Areas:Automotive sector｜Laptop case｜Consumer goods sector｜Wire and cable applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			耐热
Other performance	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index	干	ASTM D-2863	26	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-2
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ASTM D2863	26	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	湿		2.5	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	干(湿)	ASTM D-785	80(55)	M Scale
Rockwell hardness	Rockwell hardness	干(湿)	ASTM D-785	120(108)	R scale
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	39(147)	J/m
bending strength	干(湿)	ASTM D-790	118(54)	Mpa
flexural coefficient	干(湿)	ASTM D-790	2.8(1.2)	GPa
tensile strength	干(湿)	ASTM D-638	79(57)	Mpa
Elongation at Break	干(湿)	ASTM D-638	50(250)	%
Tensile modulus	23°C	ISO 527-2	3000	Mpa
tensile strength		ASTM D638	79.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	82.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.0	%
elongation	Break	ASTM D638	50	%
Tensile strain	Break,23°C	ISO 527-2	--	%
Bending modulus		ASTM D790	2800	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	2700	Mpa
bending strength		ASTM D790	118	Mpa
bending strength	bending strength	23°C	ISO 178	113	Mpa
Taber abraser	1000Cycles	ASTM D1044	--	mg
Elongation at Break		ASTM D638/ISO 527	50	%
elongation		ASTM D638/ISO 527	78.5	%
Bending modulus		ASTM D790/ISO 178	2790	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	118	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	干	ASTM D-696	8
specific heat	干		1670	J/(kg.k)
UL flame retardant rating	干	UL 94	V-2
Hot deformation temperature	0.46MPa,干	ASTM D-648	230	°C
thermal conductivity	干		0.2	W/(m.K)
Hot deformation temperature	1.82MPa,干	ASTM D-648	70	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0	°C
Linear coefficient of thermal expansion	MD	ASTM D696	8E-05	cm/cm/°C
specific heat			1670	J/kg/°C
thermal conductivity			0.20	W/m/K
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	230	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	190	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	70.0	°C
Combustibility (rate)		UL 94	v-2
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	8	mm/mm.℃
Hot deformation temperature	HDT	ASTM D648/ISO 75	230	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor	湿	ASTM D-1044	7
Shrinkage rate	干	旭化成方法	1.3-2.0	%
Shrinkage rate	Shrinkage rate	MD	Internal Method	1.3-2.0	%
Water absorption rate	Saturation,23°C		--	%
	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	--	%
	Water absorption rate	Water absorption rate		ASTM D570/ISO 62	2.5	%
Shrinkage rate		ASTM D955	1.3-2.0	%
density		ASTM D792/ISO 1183	1.14
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 1
Surface resistivity		ASTM D257	1E+13	ohms
Surface resistivity	Surface resistivity		IEC 60093	1E+13	ohms
Volume resistivity		ASTM D257	1E+14	ohms·cm
Volume resistivity	Volume resistivity	23°C	IEC 60093	1E+14	ohms·cm
Dielectric strength		ASTM D149	20	KV/mm
Dielectric strength	Dielectric strength		IEC 60243-1	20	KV/mm
Volume resistivity		ASTM D257/IEC 60093	10.10	Ω.cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ASTM D785	80
	Rockwell hardness	R-Sale	ASTM D785	120
		Rockwell hardness	M-Sale	ISO 2039-2	80
		Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shenzhen Jufengde	US$ 4010 /MT
Dongguan Yushengxin	US$ 4040 /MT
ASIAPLAS	US$ 4120 /MT
Dongguan Tianhong Plastic	US$ 5170 /MT

Supplier Join

Get App

Top

PA66 Leona™ 1402S ASAHI JAPAN

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index