PA66 1402S PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 ASAHI JAPAN 1402S

Injection grade

US$ 4,340 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	ASAHI JAPAN/1402S
elongation	Break	ASTM D638	50 %
Rockwell hardness	干(湿)	ASTM D-785	120(108) M Scale
bending strength	23°C	ISO 178	113 Mpa
tensile strength		ASTM D638	79.0 Mpa
bending strength	干(湿)	ASTM D-790	118(54) Mpa
bending strength			ASTM D790/ISO 178	118 kg·cm/cm(J/M)ft·lb/in
Bending modulus		ASTM D790/ISO 178	2790 kg·cm/cm(J/M)ft·lb/in
Tensile modulus	23°C	ISO 527-2	3000 Mpa
Tensile strain	Break,23°C	ISO 527-2	-- %
Taber abraser	1000Cycles	ASTM D1044	-- mg
tensile strength	Yield,23°C	ISO 527-2	82.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.0 %
elongation		ASTM D638/ISO 527	78.5 %
bending strength		ASTM D790	118 Mpa
tensile strength	干(湿)	ASTM D-638	79(57) Mpa
flexural coefficient	干(湿)	ASTM D-790	2.8(1.2) GPa
Elongation at Break		ASTM D638/ISO 527	50 %
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	39(147) J/m
Bending modulus	23°C	ISO 178	2700 Mpa
Bending modulus			ASTM D790	2800 Mpa
Elongation at Break	干(湿)	ASTM D-638	50(250) %
other	Test Condition	Test Method	ASAHI JAPAN/1402S
characteristic			耐热
Electrical performance	Test Condition	Test Method	ASAHI JAPAN/1402S
Volume resistivity	23°C	IEC 60093	1E+14 ohms·cm
Surface resistivity		ASTM D257	1E+13 ohms
Surface resistivity			IEC 60093	1E+13 ohms
Dielectric strength		IEC 60243-1	20 KV/mm
Dielectric strength			ASTM D149	20 KV/mm
Volume resistivity		ASTM D257	1E+14 ohms·cm
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 1
Volume resistivity		ASTM D257/IEC 60093	10.10 Ω.cm
thermal performance	Test Condition	Test Method	ASAHI JAPAN/1402S
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	8 mm/mm.℃
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	230 °C
UL flame retardant rating	干	UL 94	V-2
thermal conductivity			0.20 W/m/K
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
		HDT	ASTM D648/ISO 75	230 ℃（℉）
		0.46MPa,干	ASTM D-648	230 °C
		1.82MPa,干	ASTM D-648	70 °C
specific heat			1670 J/kg/°C
Linear coefficient of thermal expansion	MD	ASTM D696	8E-05 cm/cm/°C
thermal conductivity	干		0.2 W/(m.K)
Linear coefficient of thermal expansion	干	ASTM D-696	8
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	190 °C
Hot deformation temperature		1.8MPa,Unannealed	ASTM D648	70.0 °C
Combustibility (rate)		UL 94	v-2
specific heat	干		1670 J/(kg.k)
flammability	Test Condition	Test Method	ASAHI JAPAN/1402S
Extreme Oxygen Index		ASTM D2863	26 %
UL flame retardant rating	0.75mm	UL 94	V-2
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Physical properties	Test Condition	Test Method	ASAHI JAPAN/1402S
Shrinkage rate	干	旭化成方法	1.3-2.0 %
			ASTM D955	1.3-2.0 %
		MD	Internal Method	1.3-2.0 %
density		ASTM D792/ISO 1183	1.14
Water absorption rate		ASTM D570/ISO 62	2.5 %
Wear factor	湿	ASTM D-1044	7
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	-- %
Water absorption rate		Saturation,23°C		-- %
hardness	Test Condition	Test Method	ASAHI JAPAN/1402S
Rockwell hardness	M-Sale	ISO 2039-2	80
		R-Sale	ASTM D785	120
		M-Sale	ASTM D785	80
		R-Sale	ISO 2039-2	120
Basic Performance	Test Condition	Test Method	ASAHI JAPAN/1402S
Water absorption rate	湿		2.5 %
Other performance	Test Condition	Test Method	ASAHI JAPAN/1402S
Extreme Oxygen Index	干	ASTM D-2863	26 %
impact performance	Test Condition	Test Method	ASAHI JAPAN/1402S
Impact strength of simply supported beam without notch		ISO 179	NoBreak