PA66 Amilan® CM3001-N TORAY JAPAN
266
- Unit Price:US$ 3,842 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:74.7MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:PA66 Vydyne® 21SPC ASCEND USA
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Automotive sector｜Electrical components｜Electrical field｜Electronic field｜Electrical appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 119 | |
| R计秤,80°C | 97 -- |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 注塑级、标准级 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 265 ℃（℉） | ||
| 差示扫描测热计DSC法 | 265 °C | ||
| thermal conductivity | 无水｜0.21 Kcal/m.hr.°C | ||
| 2.5%水｜- Kcal/m.hr.°C | |||
| Linear coefficient of thermal expansion | ASTM D-696 | 无水｜9-10 10-5cm/cm | |
| ASTM D-696 | 2.5%水｜- 10-5cm/cm | ||
| specific heat | 无水｜0.4 Cal/g.°C | ||
| 2.5%水｜- Cal/g.°C | |||
| UL-94 flame retardant grade | 1/16" | UL 94 | 无水｜V-2 |
| 1/16" | UL 94 | 2.5%水 ｜- | |
| Heat Deflection Temperature | 18.6kg/cm2 | ASTM D-648 | 无水｜220 °C |
| 18.6kg/cm2 | ASTM D-648 | 2.5%水｜- °C | |
| 4.6kg/cm2 | ASTM D-648 | 无水｜220 °C | |
| 0.45MPa,未退火 | °C | 220 -- | |
| melting temperature | °C | 265 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 9.0E-5到1.0E-4 -- |
| specific heat | J/kg/°C | 2100 -- | |
| thermal conductivity | W/m/K | 0.32 -- | |
| Heat Deflection Temperature | 4.6kg/cm2 | ASTM D-648 | 2.5%水｜- °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | V-2 -- |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 无水｜1.2 % |
| 23℃，24小时 | ASTM D-570 | 2.5%水｜- % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | 无断裂 -- | |
| -40°C | 无断裂 -- |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13-1.14 | |
| Taber abraser | 1000g,CS-17 | ASTM D-1044 | 无水｜8 mg/1000次 |
| 1000g,CS-17 | ASTM D-1044 | 2.5%水｜- mg/1000次 | |
| shrinkage rate | MD：1.00mm3 | % | 0.80-1.5 -- |
| MD：3.00mm4 | % | 1.5-2.2 -- | |
| Water absorption rate | 23°C,24hr | % | 1.2 -- |
| 饱和,23°C | % | 8.0 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | 1/8" | ASTM D-150 | 无水｜128 |
| 1/8" | ASTM D-150 | 2.5%水｜- | |
| Dissipation Factor | 103Hz | ASTM D-150 | 无水｜0.03 |
| 103Hz | ASTM D-150 | 2.5%水｜- | |
| dielectric strength | 1/8" | ASTM D-149 | 无水｜18 KV/mm |
| 1/8" | ASTM D-149 | 2.5%水｜- KV/mm | |
| dielectric constant | 103Hz | ASTM D-150 | 无水｜3.9 |
| 103Hz | ASTM D-150 | 2.5%水｜- | |
| volume resistivity | ASTM D-257 | 无水｜1014-1015 Ω.cm | |
| ASTM D-257 | 2.5%水｜1011-1012 Ω.cm | ||
| dielectric constant | 106Hz | ASTM D-150 | 无水｜3.3 |
| 106Hz | ASTM D-150 | 2.5%水｜3.8 | |
| Dissipation Factor | 106Hz | ASTM D-150 | 无水｜0.02 |
| 106Hz | ASTM D-150 | 2.5%水｜0.07 | |
| Compared to the Leakage Traceability Index (CTI) | UL 746 | 无水｜≤60 V | |
| dielectric constant | 50HZ | ASTM D-150 | 无水｜4 |
| 50HZ | ASTM D-150 | 2.5%水｜- | |
| Compared to the Leakage Traceability Index (CTI) | UL 746 | 2.5%水｜- V | |
| Dissipation Factor | 50Hz | ASTM D-150 | 无水｜0.03 |
| 50Hz | ASTM D-150 | ≤60｜- | |
| volume resistivity | ohms·cm | 1.0E+14-1.0E+15 1.0E+12到1.0E+13 | |
| dielectric strength | kV/mm | 18 -- | |
| dielectric constant | 23°C,50Hz | 4.00 7.50 | |
| 23°C,1kHz | 3.90 6.50 | ||
| 23°C,1MHz | 3.30 3.80 | ||
| Dissipation Factor | 23°C,50Hz | 0.030 0.060 | |
| 23°C,1kHz | 0.030 0.060 | ||
| 23°C,1MHz | 0.020 0.070 | ||
| arc resistance | sec | 130 -- | |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | -- |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | 23℃ | ASTM D-790 | 无水｜1150 kg/cm2 |
| 23℃ | ASTM D-790 | 2.5%水｜650 kg/cm2 | |
| tensile strength | 230℃，断裂 | ASTM D-638 | 无水｜700 kg/cm2 |
| 230℃，断裂 | ASTM D-638 | 2.5%水｜730 kg/cm2 | |
| bending strength | -40℃ | ASTM D-790 | 无水｜1450 kg/cm2 |
| -40℃ | ASTM D-790 | 2.5%水｜1300 kg/cm2 | |
| Impact strength of cantilever beam gap | 23℃，无缺口1/8 | 无水｜无断裂 kg.cm/cm | |
| 23℃，无缺口1/8 | 2.5%水｜- kg.cm/cm | ||
| tensile strength | 80℃，屈服 | ASTM D-638 | 无水｜430 kg/cm2 |
| 80℃，屈服 | ASTM D-638 | 2.5%水｜400 kg/cm2 | |
| -40℃，屈服 | ASTM D-638 | 无水｜1150 kg/cm2 | |
| -40℃，屈服 | ASTM D-638 | 2.5%水｜1100 kg/cm2 | |
| flexural modulus | -40℃ | ASTM D-790 | 无水｜44000 kg/cm2 |
| -40℃ | ASTM D-790 | 2.5%水｜42000 kg/cm2 | |
| Rockwell hardness | 23℃ | ASTM D-785 | 无水｜97 R |
| 23℃ | ASTM D-785 | 2.5%水｜- R | |
| tensile strength | 23℃，屈服 | ASTM D-638 | 无水｜800 kg/cm2 |
| 23℃，屈服 | ASTM D-638 | 2.5%水｜530 kg/cm2 | |
| Elongation at break | 23℃ | ASTM D-638 | 无水｜110 % |
| 23℃ | ASTM D-638 | 2.5%水｜< 200 % | |
| shearing strength | 23℃ | ASTM D-732 | 无水｜790 kg/cm2 |
| 23℃ | ASTM D-732 | 2.5%水｜770 kg/cm2 | |
| flexural modulus | 23℃ | ASTM D-790 | 无水｜29000 kg/cm2 |
| 23℃ | ASTM D-790 | 2.5%水｜14000 kg/cm2 | |
| 80℃ | ASTM D-790 | 无水｜9000 kg/cm2 | |
| 80℃ | ASTM D-790 | 2.5%水｜5000 kg/cm2 | |
| Impact strength of cantilever beam gap | -40℃，V缺口1/2 | 无水｜3.5 kg.cm/cm | |
| -40℃，V缺口1/2 | 2.5%水｜- kg.cm/cm | ||
| 23℃，V缺口1/2 | 无水｜5 kg.cm/cm | ||
| 23℃，V缺口1/2 | 2.5%水｜28 kg.cm/cm | ||
| bending strength | 80℃ | ASTM D-790 | 无水｜640 kg/cm2 |
| 80℃ | ASTM D-790 | 2.5%水｜400 kg/cm2 | |
| compressive strength | 23℃ | ASTM D-695 | 无水｜910 kg/cm2 |
| 23℃ | ASTM D-695 | 2.5%水｜- kg/cm2 | |
| Rockwell hardness | 23℃ | ASTM D-785 | 无水｜119 R |
| 23℃ | ASTM D-785 | 2.5%水｜100 R | |
| tensile strength | -40°C | 115 MPa | |
| 23°C | MPa | 80.0 50.0 | |
| 80°C | MPa | 40.0 40.0 | |
| Tensile strain | 屈服,23°C | % | 1.5 -- |
| 断裂,23°C | % | 25 | |
| flexural modulus | -40°C | MPa | 4300 4100 |
| 23°C | MPa | 2800 1400 | |
| 80°C | MPa | 900 500 | |
| bending strength | -40°C | 140 MPa | |
| 23°C | MPa | 115 65.0 | |
| 80°C | MPa | 65.0 40.0 | |
| compression stress | 23°C | MPa | 90.0 -- |
| shear strength | 23°C | MPa | 80.0 75.0 |
| Taber abraser | 1000Cycles | mg | 8.00 -- |
| Friction coefficient - vs. Metal | 0.15to0.20 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.