Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3001-N TORAY JAPAN
Amilan®
Automotive sector,Electrical components,Electrical field,Electronic field,Electrical appliances
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | 无断裂 -- | |
| -40°C | 无断裂 -- |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 119 | |
| R计秤,80°C | 97 -- |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 2.5%水｜- % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| tensile strength | 230℃，断裂 | ASTM D-638 | 2.5%水｜730 kg/cm2 |
| Taber abraser | 1000Cycles | mg | 8.00 -- |
| tensile strength | 23°C | MPa | 80.0 50.0 |
| bending strength | 23℃ | ASTM D-790 | 2.5%水｜650 kg/cm2 |
| tensile strength | 23℃，屈服 | ASTM D-638 | 2.5%水｜530 kg/cm2 |
| Flexural modulus | -40°C | MPa | 4300 4100 |
| 80℃ | ASTM D-790 | 2.5%水｜5000 kg/cm2 | |
| compressive strength | 23℃ | ASTM D-695 | 2.5%水｜- kg/cm2 |
| bending strength | 23°C | MPa | 115 65.0 |
| tensile strength | 80°C | MPa | 40.0 40.0 |
| Tensile strain | 断裂,23°C | % | 25 |
| bending strength | 80°C | MPa | 65.0 40.0 |
| shear strength | 23°C | MPa | 80.0 75.0 |
| shearing strength | 23℃ | ASTM D-732 | 2.5%水｜770 kg/cm2 |
| bending strength | -40°C | 140 MPa | |
| Impact strength of cantilever beam gap | 23℃，V缺口1/2 | 2.5%水｜28 kg.cm/cm | |
| bending strength | -40℃ | ASTM D-790 | 2.5%水｜1300 kg/cm2 |
| Flexural modulus | -40℃ | ASTM D-790 | 2.5%水｜42000 kg/cm2 |
| bending strength | 80℃ | ASTM D-790 | 2.5%水｜400 kg/cm2 |
| compression stress | 23°C | MPa | 90.0 -- |
| Flexural modulus | 23℃ | ASTM D-790 | 2.5%水｜14000 kg/cm2 |
| 80°C | MPa | 900 500 | |
| tensile strength | 80℃，屈服 | ASTM D-638 | 2.5%水｜400 kg/cm2 |
| -40°C | 115 MPa | ||
| Tensile strain | 屈服,23°C | % | 1.5 -- |
| Impact strength of cantilever beam gap | 23℃，无缺口1/8 | 2.5%水｜- kg.cm/cm | |
| elongation at break | 23℃ | ASTM D-638 | 2.5%水｜< 200 % |
| tensile strength | -40℃，屈服 | ASTM D-638 | 2.5%水｜1100 kg/cm2 |
| Impact strength of cantilever beam gap | -40℃，V缺口1/2 | 2.5%水｜- kg.cm/cm | |
| Rockwell hardness | 23℃ | ASTM D-785 | 2.5%水｜100 R |
| Flexural modulus | 23°C | MPa | 2800 1400 |
| Friction coefficient - vs. Metal | 0.15to0.20 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| arc resistance | 1/8" | ASTM D-150 | 2.5%水｜- |
| dielectric strength | 1/8" | ASTM D-149 | 2.5%水｜- KV/mm |
| Dissipation Factor | 106Hz | ASTM D-150 | 2.5%水｜0.07 |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | -- |
| Dissipation Factor | 103Hz | ASTM D-150 | 2.5%水｜- |
| dielectric constant | 23°C,1kHz | 3.90 6.50 | |
| 103Hz | ASTM D-150 | 2.5%水｜- | |
| Compared to the Leakage Traceability Index (CTI) | UL 746 | 2.5%水｜- V | |
| dielectric constant | 106Hz | ASTM D-150 | 2.5%水｜3.8 |
| dielectric strength | kV/mm | 18 -- | |
| dielectric constant | 23°C,50Hz | 4.00 7.50 | |
| 23°C,1MHz | 3.30 3.80 | ||
| Dissipation Factor | 23°C,50Hz | 0.030 0.060 | |
| 23°C,1kHz | 0.030 0.060 | ||
| arc resistance | sec | 130 -- | |
| Dissipation Factor | 50Hz | ASTM D-150 | ≤60｜- |
| Volume resistivity | ASTM D-257 | 2.5%水｜1011-1012 Ω.cm | |
| dielectric constant | 50HZ | ASTM D-150 | 2.5%水｜- |
| Dissipation Factor | 23°C,1MHz | 0.020 0.070 | |
| Volume resistivity | ohms·cm | 1.0E+14-1.0E+15 1.0E+12到1.0E+13 |
| other | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| characteristic | 注塑级、标准级 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13-1.14 |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | V-2 -- |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | % | 8.0 -- |
| Shrinkage rate | MD：1.00mm3 | % | 0.80-1.5 -- |
| MD：3.00mm4 | % | 1.5-2.2 -- | |
| Taber abraser | 1000g,CS-17 | ASTM D-1044 | 2.5%水｜- mg/1000次 |
| Water absorption rate | 23°C,24hr | % | 1.2 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM3001-N |
|---|---|---|---|
| thermal conductivity | 2.5%水｜- Kcal/m.hr.°C | ||
| specific heat | 2.5%水｜- Cal/g.°C | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 220 -- |
| melting temperature | °C | 265 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 9.0E-5到1.0E-4 -- |
| ASTM D-696 | 2.5%水｜- 10-5cm/cm | ||
| specific heat | J/kg/°C | 2100 -- | |
| Heat distortion temperature | 4.6kg/cm2，HDT | ASTM D-648 | 2.5%水｜- °C |
| melting temperature | 差示扫描测热计DSC法 | 265 °C | |
| UL-94 flame retardant grade | 1/16" | UL 94 | 2.5%水 ｜- |
| thermal conductivity | W/m/K | 0.32 -- | |
| melting temperature | 265 ℃（℉） | ||
| Heat distortion temperature | 18.6kg/cm2，HDT | ASTM D-648 | 2.5%水｜- °C |