PA66 Vydyne® 67R ASCEND USA

284

Unit Price:US$ 5,120 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
Dongguan Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
squeeze out	Test Condition	Test Method	Test Result	Test Unit
Temperature in Zone 1 of the material cylinder			280 to 295	°C
Temperature in Zone 2 of the material cylinder			280 to 295	°C
Temperature in Zone 3 of the material cylinder			280 to 295	°C
Temperature in Zone 4 of the material cylinder			280 to 295	°C
Temperature in Zone 5 of the material cylinder			280 to 295	°C
Melt Temperature			270 to 295	°C
Oral mold temperature			270 to 295	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Poisson's ratio		ISO 527-2	0.40
bending strength	23°C	ISO 178	80.0	Mpa
Bending modulus	23°C	ISO 178	3000	Mpa
Nominal tensile fracture strain	23°C	ISO 527-2	40	%
Tensile strain	Yield, 23°C	ISO 527-2	5.0	%
tensile strength	Break, 23°C	ISO 527-2	55.0	Mpa
tensile strength	tensile strength	Yield, 23°C	ISO 527-2	85.0	Mpa
Tensile modulus	23°C	ISO 527-2	2850	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature at the rear of the barrel			280 to 310	°C
Temperature in the middle of the barrel			280 to 310	°C
Suggested maximum material return ratio			25	%
Suggested maximum moisture content			0.050 to 0.10	%
drying time			4.0	hr
drying temperature			60 to 75	°C
Temperature at the front of the material cylinder			280 to 310	°C
Spray nozzle temperature			280 to 310	°C
Processing (melt) temperature			285 to 305	°C
Mold temperature			65 to 95	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	1.0E-4	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	1.0E-4	cm/cm/°C
Melting temperature		ISO 11357-3	260	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	65.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	200	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.5	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	8.5	%
Shrinkage rate	Flow : 23°C, 2.00 mm	ISO 294-4	2.2	%
Shrinkage rate	Shrinkage rate	横向Flow : 23°C, 2.00 mm	ISO 294-4	2.1	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	0.750 mm	IEC 60093	1.0E+14	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shenzhen Jufengde	US$ 4810 /MT

Supplier Join

Get App

Top

PA66 Vydyne® 67R ASCEND USA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index