PA66 67R ASCEND USA
Vydyne®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASCEND USA/67R |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | ASCEND USA/67R |
|---|---|---|---|
| Tensile strain | 屈服, 23°C | ISO 527-2 | 5.0 % |
| Flexural modulus | 23°C | ISO 178 | 3000 Mpa |
| Bending stress | 23°C | ISO 178 | 80.0 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2850 Mpa |
| Tensile stress | 屈服, 23°C | ISO 527-2 | 85.0 Mpa |
| 断裂, 23°C | ISO 527-2 | 55.0 Mpa | |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 40 % |
| Poisson's ratio | ISO 527-2 | 0.40 |
| Electrical performance | Test Condition | Test Method | ASCEND USA/67R |
|---|---|---|---|
| Volume resistivity | 0.750 mm | IEC 60093 | 1.0E+14 ohms·cm |
| squeeze out | Test Condition | Test Method | ASCEND USA/67R |
|---|---|---|---|
| 280 到 295 °C | |||
| die temperature | 270 到 295 °C | ||
| Temperature in Zone 3 of the material cylinder | 280 到 295 °C | ||
| Temperature in Zone 5 of the material cylinder | 280 到 295 °C | ||
| Melt Temperature | 270 到 295 °C |
| physical property | Test Condition | Test Method | ASCEND USA/67R |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.5 % |
| Shrinkage rate | 横向流量 : 23°C, 2.00 mm | ISO 294-4 | 2.1 % |
| 流量 : 23°C, 2.00 mm | ISO 294-4 | 2.2 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 8.5 % |
| Thermal performance | Test Condition | Test Method | ASCEND USA/67R |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 260 °C | |
| 流动 : 23 到 55°C, 2.00 mm | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 200 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 65.0 °C | |
| 横向 : 23 到 55°C, 2.00 mm | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| injection | Test Condition | Test Method | ASCEND USA/67R |
|---|---|---|---|
| Temperature | 65 到 95 °C | ||
| Temperature at the rear of the barrel | 280 到 310 °C | ||
| Processing (melt) temperature | 285 到 305 °C | ||
| drying temperature | 60 到 75 °C | ||
| Temperature at the front of the material cylinder | 280 到 310 °C | ||
| drying time | 4.0 hr | ||
| Suggested maximum moisture content | 0.050 到 0.10 % | ||
| Suggested maximum recycled material ratio | 25 % | ||
| Spray nozzle temperature | 280 到 310 °C | ||
| Temperature in the middle of the barrel | 280 到 310 °C |