PBT CELANEX® 3316 ED3002 CELANESE USA
216
- Unit Price:US$ 5,536 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Automotive sector｜Electronic and electrical accessories
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 89 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 220 °C |
| 0.45MPa,退火 | ASTM D648 | 221 °C | |
| 1.8MPa,未退火 | ASTM D648 | 206 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 208 °C | |
| 8.0MPa,未退火 | ISO 75-2/C | 165 °C | |
| vicat | ISO 306/B50 | 225 °C | |
| melting temperature | ASTM D3418 | 225 °C | |
| ISO 11357-3 | 225 °C | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7.7E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| 1.5mm | UL 94 | 5VA | |
| Limiting Oxygen Index | ISO 4589-2 | 30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 42 kJ/m² |
| 23°C | ISO 179/1eU | 59 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.7 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 1MHz | ASTM D150 | 3.50 |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| 1MHz | IEC 60250 | 2.90 | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.020 |
| 100Hz | IEC 60250 | 3.3E-03 | |
| 1MHz | IEC 60250 | 0.015 | |
| arc resistance | ASTM D495 | 106 sec | |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | PLC 2 | |
| IEC 60112 | PLC 2 | ||
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| volume resistivity | ASTM D257 | 2E+16 ohms·cm | |
| IEC 60093 | 1E+15 ohms·cm | ||
| dielectric strength | ASTM D149 | 20 KV/mm | |
| IEC 60243-1 | 34 KV/mm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.16 % |
| density | ASTM D792 | 1.66 g/cm³ | |
| ISO 1183 | 1.66 g/cm³ | ||
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 7.00 cm3/10min |
| shrinkage rate | MD | ASTM D955 | 0.30-0.50 % |
| TD | ISO 294-4 | 0.80-1.3 % | |
| MD | ISO 294-4 | 0.10-0.80 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C | ASTM D638 | 9650 Mpa |
| ISO 527-2/1A/1 | 10700 Mpa | ||
| tensile strength | 断裂,23°C | ASTM D638 | 134 Mpa |
| 断裂 | ISO 527-2/1A/5 | 135 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 2.5 % |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.5 % |
| flexural modulus | 23°C | ISO 178 | 10300 Mpa |
| bending strength | 23°C | ISO 178 | 200 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.