PBT 3316 ED3002 CELANESE USA
CELANEX®
Automotive sector,Electronic and electrical accessories
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/3316 ED3002 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.5 kJ/m² |
| -30°C | ISO 179/1eA | 8.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 59 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.7 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 42 kJ/m² |
| hardness | Test Condition | Test Method | CELANESE USA/3316 ED3002 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 89 |
| thermal performance | Test Condition | Test Method | CELANESE USA/3316 ED3002 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 208 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C | |
| 0.45MPa,退火，HDT | ASTM D648 | 221 °C | |
| vicat | ISO 306/B50 | 225 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7.7E-05 cm/cm/°C |
| melting temperature | ASTM D3418 | 225 °C | |
| Heat Deflection Temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 165 °C |
| melting temperature | ISO 11357-3 | 225 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ASTM D648 | 206 °C |
| mechanical properties | Test Condition | Test Method | CELANESE USA/3316 ED3002 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 200 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 10700 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 2.5 % |
| Tensile modulus | 23°C | ASTM D638 | 9650 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.5 % |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 135 Mpa |
| 断裂,23°C | ASTM D638 | 134 Mpa | |
| flexural modulus | 23°C | ISO 178 | 10300 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/3316 ED3002 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.020 |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | PLC 2 | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| Dissipation Factor | 100Hz | IEC 60250 | 3.3E-03 |
| dielectric constant | 1MHz | ASTM D150 | 3.50 |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| volume resistivity | ASTM D257 | 2E+16 ohms·cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| arc resistance | ASTM D495 | 106 sec | |
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 20 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| Physical properties | Test Condition | Test Method | CELANESE USA/3316 ED3002 |
|---|---|---|---|
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 7.00 cm3/10min |
| density | ISO 1183 | 1.66 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 0.80-1.3 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.16 % |
| shrinkage rate | MD | ISO 294-4 | 0.10-0.80 % |
| MD | ASTM D955 | 0.30-0.50 % | |
| density | ASTM D792 | 1.66 g/cm³ |
| flammability | Test Condition | Test Method | CELANESE USA/3316 ED3002 |
|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| 1.5mm | UL 94 | 5VA | |
| Limiting Oxygen Index | ISO 4589-2 | 30 % |