Material Properties:Low temperature resistance｜High temperature resistance｜high strength｜High impact resistance｜Resistance to stress cracking
Application Areas:Plate｜sheet
Color:--
Grade:Impact resistant grade

Technical Data Sheet Compare

processability	Test Condition	Test Method	Test Result
Injection molding melt temperature			180-260 °C
Melt Temperature			180-240 °C
Injection mold temperature			10-60 °C

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	HDT	ISO 75	88 °C
UL flame retardant rating		UL 94	HB
vicat		ISO 306	90 °C
vicat	vicat		ASTM D1525/ISO R306	90 ℃（℉）

other	Test Condition	Test Method	Test Result
characteristic			高冲击.高刚度。
Color			无色

Basic performance	Test Method	Test Result
Water absorption rate	ISO 62	<0.1 %
density	ISO 1183	1.05 g/cm³
melt mass-flow rate	ISO 1133	3.2 cm3/10min

Other performance	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527	1600 Mpa

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 6093	>1014 Ω.cm

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate			0.4-0.7 %
Water absorption rate		ASTM D570/ISO 62	10.5 %

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23℃	ISO 179/1eA	11 kJ/m²
Tensile stress		ISO 527	21 Mpa
Elongation at break		ISO 527	40 %
bending strength		ISO 178	32 Mpa
Impact strength of cantilever beam gap	23℃	ISO 180	10 kJ/m²
Rockwell hardness		ASTM D-785	70 L标尺
Rockwell hardness	Rockwell hardness		ASTM D785	70
bending strength		ASTM D790/ISO 178	32 kg/cm²(MPa)[Lb/in²]
Elongation at break		ASTM D638/ISO 527	40 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.