HIPS 2710 BASF-YPC
--
Plate、sheet
Low temperature resistanc、High temperature resistan、high strength、High impact resistance、Resistance to stress crac
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Other performanceTest ConditionTest MethodBASF-YPC/2710
Tensile modulus of elasticityISO 5271600 Mpa
Basic performanceTest ConditionTest MethodBASF-YPC/2710
Water absorption rateISO 62<0.1 %
melt mass-flow rateISO 11333.2 cm3/10min
densityISO 11831.05 g/cm³
Mechanical propertiesTest ConditionTest MethodBASF-YPC/2710
bending strengthASTM D790/ISO 17832 kg/cm²(MPa)[Lb/in²]
ISO 17832 Mpa
Rockwell hardnessASTM D-78570 L标尺
Shear beam notch impact strength23℃ISO 179/1eA11 kJ/m²
tensile yield stressISO 52721 Mpa
tensile elongation at breakISO 52740 %
Rockwell hardnessASTM D78570
Tensile elongation at break (elongation at break)ASTM D638/ISO 52740 %
Impact strength of cantilever beam gap23℃ISO 18010 kJ/m²
Electrical performanceTest ConditionTest MethodBASF-YPC/2710
Volume resistivityIEC6093>1014 Ω.cm
otherTest ConditionTest MethodBASF-YPC/2710
高冲击，高刚度。
colour无色
Physical propertiesTest ConditionTest MethodBASF-YPC/2710
Water absorption rateASTM D570/ISO 6210.5 %
processabilityTest ConditionTest MethodBASF-YPC/2710
Extrusion molding melt temperature180-240 °C
Injection molding mold temperature10-60 °C
180-260 °C
physical property Test ConditionTest MethodBASF-YPC/2710
Shrinkage rate of molded products0.4-0.7 %
Thermal performanceTest ConditionTest MethodBASF-YPC/2710
Flame retardancyUL 94HB
vicatISO 30690 °C
ASTM D1525/ISO R30690 ℃（℉）
ISO 7588 °C