ABS UMG ABS® TM-25 UMG JAPAN
262
- Unit Price:US$ 3,060 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:59.3MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Heat resistant grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 4.00 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.50-0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 112 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | 2400 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 9 kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ASTM D638/ISO 527 | 2300 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 46 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 112 | |
| Flexural modulus | ASTM D790/ISO 178 | 2400 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 70 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 18 kg·cm/cm(J/M)ft·lb/in | |
| Charpy Notched Impact Strength | 18 kJ/m² | ||
| Tensile modulus | ISO 527-2 | 2300 Mpa | |
| tensile strength | ISO 527-2 | 46.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ISO 178 | 70.0 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.06 | |
| Shrinkage rate | ASTM D955 | 0.5-0.7 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 4 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | 1.5 HB | |
| Heat distortion temperature | ASTM D648/ISO 75 | 98 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 9 mm/mm.℃ | |
| Heat distortion temperature | 98 °C | ||
| UL flame retardant rating | UL 94 | HB | |
| Heat distortion temperature | ISO 75-2/Af | 98.0 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.