Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS TM-25 UMG JAPAN
UMG ABS®
Automotive sector
High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodUMG JAPAN/TM-25
Rockwell hardnessR计秤,23°CISO 2039-2112
Basic performanceTest ConditionTest MethodUMG JAPAN/TM-25
Flexural modulus2400 Mpa
Mechanical propertiesTest ConditionTest MethodUMG JAPAN/TM-25
Impact strength of cantilever beam gapASTM D256/ISO 17918 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 17870 kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength18 kJ/m²
Flexural modulusASTM D790/ISO 1782400 kg/cm²(MPa)[Lb/in²]
bending strength23°CISO 17870.0 Mpa
Flexural modulus23°CISO 1782400 Mpa
Tensile modulusASTM D638/ISO 5272300 kg/cm²(MPa)[Lb/in²]
23°CISO 527-22300 Mpa
Rockwell hardnessASTM D785112
tensile strength ASTM D638/ISO 52746 kg/cm²(MPa)[Lb/in²]
23°CISO 527-246.0 Mpa
Physical propertiesTest ConditionTest MethodUMG JAPAN/TM-25
Shrinkage rateASTM D9550.5-0.7 %
densityASTM D792/ISO 11831.06
melt mass-flow rateASTM D1238/ISO 11334 g/10min
flammabilityTest ConditionTest MethodUMG JAPAN/TM-25
UL flame retardant rating1.5mmUL 94HB
physical property Test ConditionTest MethodUMG JAPAN/TM-25
Shrinkage rateMD：23°CISO 294-40.50-0.70 %
Melt volume flow rate220°C/10.0kgISO 11334.00 cm3/10min
Thermal performanceTest ConditionTest MethodUMG JAPAN/TM-25
Combustibility (rate)UL 941.5 HB
Heat distortion temperatureHDT98 °C
1.8MPa,未退火，HDTISO 75-2/Af98.0 °C
HDTASTM D648/ISO 7598 ℃（℉）
Linear coefficient of thermal expansionMDISO 11359-29E-05 cm/cm/°C
ASTM D696/ISO 113599 mm/mm.℃
UL flame retardant ratingUL 94HB