PC LEXAN™ EXL5689-739 SABIC INNOVATIVE US
96
Unit Price:$3416 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 38MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility｜Ductility at low temperat｜Short molding cycle
- Application Areas:Electronic and Electrical｜Aerospace Applications｜lens
- Color:--
- Grade:--
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 9.0 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 8.00 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.60 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 132 °C |
| Vicat Softening Temperature | ASTMD152510 | 146 °C | |
| -- | ISO306/B50 | 145 °C | |
| -- | ISO306/B120 | 146 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 4.7E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 4.7E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | HB |
| 1.2mm | UL94 | V-1 | |
| 1.5mm | UL94 | V-0 | |
| GlowWireFlammability | 1.1mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 °C |
| 2.0mm | IEC60695-2-13 | 825 °C | |
| 2.5mm | IEC60695-2-13 | 825 °C | |
| 3.0mm | IEC60695-2-13 | 825 °C |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Comparative Tracking Index | CTI | UL746 | PLC 3 |
| IEC60112 | 175 V |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Stress | 屈服 | ISO527-2/5 | 54.0 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 44.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 46.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.4 % |
| Tensile Strain | 屈服 | ISO527-2/5 | 4.4 % |
| Tensile Elongation | 断裂 | ASTMD638 | 15 % |
| Tensile Strain | 断裂 | ISO527-2/5 | 13 % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 3150 Mpa |
| ISO178 | 3400 Mpa | ||
| Flexural Strength | ISO178 | 96.0 Mpa | |
| Tensile Modulus | ASTMD638 | 3500 Mpa | |
| ISO527-2/1 | 3600 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 55.0 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 97.0 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NoBreak |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 40.0 J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 15 kJ/m² |
| 23°C | ISO179/1eA | 30 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| 23°C | ISO179/1eU | NoBreak | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| 23°C | ISO180/1A | 25 kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.