Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL5689-739 SABIC INNOVATIVE US
LEXAN™
Electronic and Electrical、Aerospace Applications、lens
High mobility、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL5689-739 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 132 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B50 | 145 °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 4.7E-05 cm/cm/°C | |
| Vicat Softening Temperature | ASTMD152510 | 146 °C | |
| -- | ISO306/B120 | 146 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 4.7E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL5689-739 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 3150 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 15 % |
| Tensile Strain | 断裂 | ISO527-2/5 | 13 % |
| Tensile Modulus | ISO527-2/1 | 3600 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 55.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 46.0 Mpa |
| Flexural Modulus | ISO178 | 3400 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 97.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.4 % |
| Flexural Strength | ISO178 | 96.0 Mpa | |
| Tensile Modulus | ASTMD638 | 3500 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 44.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/5 | 4.4 % |
| Tensile Stress | 屈服 | ISO527-2/5 | 54.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/EXL5689-739 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.60 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 9.0 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 8.00 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL5689-739 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 15 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 40.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 30 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NoBreak |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 25 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/EXL5689-739 |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | HB |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 °C |
| 3.0mm | IEC60695-2-13 | 825 °C | |
| 2.0mm | IEC60695-2-13 | 825 °C | |
| Flame Rating | 1.5mm | UL94 | V-0 |
| 1.2mm | UL94 | V-1 | |
| Glow Wire Ignition Temperature | 2.5mm | IEC60695-2-13 | 825 °C |
| GlowWireFlammability | 1.1mm | IEC60695-2-12 | 960 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL5689-739 |
|---|---|---|---|
| Comparative Tracking Index | IEC60112 | 175 V | |
| CTI | UL746 | PLC 3 |