PC TARFLON™ AZ1900T IDEMITSU JAPAN
254
Unit Price:$6562 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Automotive Applications Home appliance components
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.20 | ||
| Shrinkage rate | ASTM D955 | 0.5~0.7 | % | |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 5.00 | cm3/10min |
| SpiralFlow2. | 内部方法 | 48.0 | CM | |
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.50to0.70 | % |
| MD:2.00mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.23 | % |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 18.0 | cm3/10min |
| Spiral Flow 3, | 内部方法 | 29.0 | CM | |
| Shrinkage rate | Across Flow : 2.00 mm | 内部方法 | 0.50 到 0.70 | % |
| 流量 : 2.00 mm | 内部方法 | 0.50 到 0.70 | % | |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.23 | % |
| Melt Volume-Flow Rate (MVR) | MVR | ISO 1133 | 5 | cm3/10min |
| Shrinkage rate | TD | Internal Method | 0.5-0.7 | % |
| MD: 2.00 mm | Internal Method | 0.5-0.7 | % | |
| Water absorption rate | Equilibrium, 23℃, 50% RH | ISO 62 | 0.23 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Yield | ISO 527-2 | 65 | Mpa |
| Fracture rate | ISO 527-2 | 70 | % | |
| Bending modulus | ISO 178 | 2300 | Mpa | |
| bending strength | ISO 178 | 90 | Mpa | |
| Impact strength of simply supported beam gap | ISO 179 | 65 | kJ/m² | |
| Rockwell hardness | M -Sale | ISO 2039-2 | 50 | |
| R -Sale | ISO 2039-2 | 120 | ||
| tensile strength | Yield | ISO 527-2 | 65.0 | Mpa |
| Nominal tensile fracture strain | ISO 527-2 | 95 | % | |
| bending strength | ISO 178 | 90.0 | Mpa | |
| tensile strength | Yield | ISO527-2 | 65.0 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 70 | % | |
| Bending modulus | ISO178 | 2300 | Mpa | |
| bending strength | ISO178 | 90.0 | Mpa | |
| Rockwell hardness | M-Sale | ISO2039-2 | 50 | |
| R-Sale | ISO2039-2 | 120 | ||
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 92 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 2300 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 68 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 64 | % | |
| Bending modulus | ASTM D790/ISO 178 | 2400 | kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 92 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 125 | °C |
| Linear expansion coefficient - flow | ASTM D696 | 0.000065 | cm/cm/℃ | |
| Flame retardant grade | 1.50 mm | UL 94 | V-0 | |
| 4.00 mm | UL 94 | 5VA | ||
| Combustibility (rate) | UL94 | V-0/1.5mm | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 131 | ℃（℉） | |
| 0.45MPa,Unannealed | ISO75-2/B | 140 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| RTIElec | UL746 | 80.0 | °C | |
| RTI Imp | UL746 | 80.0 | °C | |
| RTIStr | UL746 | 80.0 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 125 | °C |
| Linear coefficient of thermal expansion - flow | ISO 11359-2 | 6.5E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 80.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI | UL 746 | 80.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC 60243-1 | 30 | KV/mm | |
| Dielectric constant | 1 MHz | IEC 60250 | 2.85 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | ||
| Dielectric strength | IEC60243-1 | 30 | KV/mm | |
| Dielectric constant | 1MHz | IEC60250 | 2.85 | |
| 1 MHz | IEC 60250 | 2.85 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| drying time | 5.0 到 8.0 | hr | ||
| Temperature at the rear of the barrel | 260 到 300 | °C | ||
| Temperature in the middle of the barrel | 260 到 300 | °C | ||
| Temperature at the front of the material cylinder | 260 到 300 | °C | ||
| Mold temperature | 80 到 120 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | ISO13468-1 | 85.0to89.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 | |
| ISO | >PC< |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | >PC< |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.