Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC AZ1900T IDEMITSU JAPAN
TARFLON™
Automotive Applications、Home appliance components
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/AZ1900T
Spiral Flow 3,
内部方法
CM
2
SpiralFlow2.
内部方法
CM
4
Melt Volume-Flow Rate (MVR)
MVR
ISO 1133
cm3/10min
5
Melt Volume-Flow Rate (MVR)
300°C/1.2kg
ISO1133
cm3/10min
5
Melt Volume-Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
1
Shrinkage rate
TD
Internal Method
%
0
Shrinkage rate
MD: 2.00 mm
Internal Method
%
0
Shrinkage rate
ASTM D955
%
0
Shrinkage rate
TD:2.00mm
内部方法
%
0
Shrinkage rate
MD:2.00mm
内部方法
%
0
Shrinkage rate
横向流量 : 2.00 mm
内部方法
%
0
Shrinkage rate
流量 : 2.00 mm
内部方法
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Water absorption rate
平衡, 23℃, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/AZ1900T
Nominal tensile fracture strain
ISO527-2
%
7
Nominal tensile fracture strain
ISO 527-2
%
9
elongation at break
ASTM D638/ISO 527
%
9
Fracture rate
ISO 527-2
%
7
Impact strength of simply supported beam gap
ISO 179
kJ/m²
6
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
2
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
tensile strength
屈服
ISO 527-2
Mpa
6
tensile strength
屈服
ISO527-2
Mpa
6
tensile strength
屈服
ISO 527-2
Mpa
6
elongation
ASTM D638/ISO 527
%
6
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
Bending modulus
ISO 178
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ISO178
Mpa
9
bending strength
ISO 178
Mpa
9
bending strength
ISO 178
Mpa
9
Impact strength of cantilever beam gap
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
8
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
9
Thermal performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/AZ1900T
RTI
UL 746
°C
8
RTI Elec
UL 746
°C
8
RTI Imp
UL 746
°C
8
RTI Imp
UL746
°C
8
RTIElec
UL746
°C
8
RTIStr
UL746
°C
8
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
1
Linear expansion coefficient - flow
ASTM D696
cm/cm/℃
0
Linear coefficient of thermal expansion - flow
ISO 11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
6
Electrical performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/AZ1900T
Dielectric strength
IEC60243-1
KV/mm
3
Dielectric strength
IEC 60243-1
KV/mm
3
optical performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/AZ1900T
Light transmittance
ISO13468-1
%
8