PC PANLITE® LN-2250Y TEIJIN JAPAN
244
Unit Price:$5028 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 38.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜optical performance
- Application Areas:Optical level
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Index of Refraction | ASTM D-542 | 1585 | |
| Density | ISO 1183 | 1200 kg/m | |
| Moisture Absorption | 24hr in 23℃ | ASTM D-570 | 0.20 % |
| Transmittance | 3mm thick | ASTM D-1003 | 88 % |
| Melt Mass-Flow Rate | 300℃/1.2Kg | ISO1133 | 11.0 cm3/10min |
| Modeling Shrinkage | MD4.00mm | ISO294-4 | 0.50-0.70 % |
| TD4.00 | ISO294-4 | 0.50-0.70 % | |
| Moisture Absorption | (23°C,24hr) | ISO62 | 0.20 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat Softening Temperature | 50℃/h 50N | ISO 308 | 148 °C |
| Coefficient of Linear Thermal Expansion | 平行方向 | ISO 11359-2 | 0.7 |
| 垂直方向 | ISO 11359-2 | 0.7 | |
| Deflection Temperature Under Load? | 0.45MPa | ISO 75-1 and ISO 75-2 | 141 °C |
| Temperature Index | 电学式，厚度1.47mm | UL 746B | 125 °C |
| 冲击式，厚度1.47mm | UL 746B | 115 °C | |
| 非冲击式，厚度1.47mm | UL 746B | 125 °C | |
| Deflection Temperature Under Load? | 1.80MPa | ISO 75-1 and ISO 75-2 | 128 °C |
| Heat Deflection Temperature | 0.45MPa未退火 | ISO75-2/Bf | 141 °C |
| 1.80MPa退火 | ISO75-2/A | 128 °C | |
| Vicat Softening Temperature | ISO306/B50 | 148 °C | |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| TD | ISO11359-2 | 7E-05 cm/cm/°C | |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 148 ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Transmittance | ASTM D1003/ISO 13468 | 88 % | |
| Index of Refraction | ASTM D542/ISO 489 | 1.585 |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Fire rating | UL-94 | 6.00mm V-0 | |
| UL-94 | 0.43mm V-2 | ||
| UL-94 | 3.00mm V-0 |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor?(Tangent) | 1MHz | IEC 60250 | 90 |
| Dielectric Constant | 100Hz | IEC 60250 | 3.1 |
| Surface Resistivity | IEC600 | >1×10 Ω | |
| Arc Resistance | IEC 60112 | 225 | |
| 短时间法 | IEC 60243-1 | 32 MV/m | |
| Volume Resistivity | IEC 60093 | >1×10 Ω.cm | |
| Dissipation Factor?(Tangent) | 100Hz | IEC 60250 | 10 |
| Dielectric Constant | 1MHz | IEC 60250 | 3 |
| Volume Resistivity | IEC60093 | >1.0E+15 Ω.cm | |
| Surface resistance | IEC60093 | >1.0E+15 Ω.cm | |
| Dielectric Constant | IEC60250 | 32 1kHz | |
| IEC60250 | 3.00 1MHz | ||
| IEC60250 | 3.10 100HZ | ||
| Dissipation Factor? | IEC60250 | 1E-03 | |
| IEC60250 | 9E-03 | ||
| 相对漏电起痕指数 | IEC60112 | 225 V | |
| Dielectric Constant | ASTM D150/IEC 60250 | 3.1 | |
| ASTM D150/IEC 60250 | 3 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Elongation (Break) | 50mm/min | ISO 527-1 and ISO 527-2 | >50 % |
| Izod Impact Strength | 没缺口 | ISO 179 | NB KJ/m |
| Tensile Modulus | 1mm/min | ISO 527-1 and ISO 527-2 | 2400 Mpa |
| Izod Impact Strength | 带缺口 | ISO 179 | 12 KJ/m |
| Flexural Strength | 2mm/min | ISO 178 | 92 Mpa |
| Tensile Stress(Yield) | 50mm/min | ISO 527-1 and ISO 527-2 | 61 Mpa |
| Tensile Elongation?(Yield) | 50mm/min | ISO 527-1 and ISO 527-2 | 6 % |
| Flexural Modulus | 2mm/min | ISO 178 | 2350 Mpa |
| Tensile Strength | 屈服，23°C | ISO527-2 | 61.0 Mpa |
| Tensile Elongation?(Break) | 屈服，23°C | ISO527-2 | 6.0 % |
| 23°C | ISO527-2 | >50 % | |
| Tensile Modulus | 23°C | ISO527-2 | 2400 Mpa |
| Flexural Strength | 23°C | ISO178 | 92.0 Mpa |
| Flexural Modulus | 23°C | ISO178 | 2350 Mpa |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 76 kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NB kJ/m² |
| Tensile Modulus | ASTM D638/ISO 527 | /2400 kg/cm²(MPa)[Lb/in²] | |
| Tensile Strength | ASTM D638/ISO 527 | /61 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | /6 % | |
| Flexural Modulus | ASTM D790/ISO 178 | /2350 kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | /92 kg/cm²(MPa)[Lb/in²] |
| Processing | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Modeling Shrinkage | 平行方向 | 本公司制订的测定法 | 0.5～0.7 % |
| 垂直方向 | 本公司制订的测定法 | 0.5～0.7 % |
| Physical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | /1200 | |
| Modeling Shrinkage | ASTM D955 | 0.5-0.7 % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.2 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.