Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LN-2250Y TEIJIN JAPAN
PANLITE®
Optical level
Flame retardant、optical performance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TEIJIN JAPAN/LN-2250Y |
|---|---|---|---|
| Temperature Index | 冲击式，厚度1.47mm | UL 746B | 115 °C |
| Heat Deflection Temperature | 0.45MPa未退火 | ISO75-2/Bf | 141 °C |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 148 ℃（℉） | |
| Temperature Index | 电学式，厚度1.47mm | UL 746B | 125 °C |
| Heat Deflection Temperature | 1.80MPa退火 | ISO75-2/A | 128 °C |
| Deflection Temperature Under Load? | 0.45MPa | ISO 75-1 and ISO 75-2 | 141 °C |
| Temperature Index | 非冲击式，厚度1.47mm | UL 746B | 125 °C |
| Vicat Softening Temperature | ISO306/B50 | 148 °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ | |
| Vicat Softening Temperature | 50℃/h 50N | ISO 308 | 148 °C |
| Coefficient of Linear Thermal Expansion | 平行方向 | ISO 11359-2 | 0.7 |
| 垂直方向 | 0.7 | ||
| MD | ISO11359-2 | 7E-05 cm/cm/°C | |
| Deflection Temperature Under Load? | 1.80MPa | ISO 75-1 and ISO 75-2 | 128 °C |
| Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | TEIJIN JAPAN/LN-2250Y |
|---|---|---|---|
| Transmittance | 3mm thick | ASTM D-1003 | 88 % |
| Index of Refraction | ASTM D-542 | 1585 | |
| Modeling Shrinkage | MD4.00mm | ISO294-4 | 0.50-0.70 % |
| Melt Mass-Flow Rate | 300℃/1.2Kg | ISO1133 | 11.0 cm3/10min |
| Density | ISO 1183 | 1200 kg/m | |
| Modeling Shrinkage | TD4.00 | ISO294-4 | 0.50-0.70 % |
| Moisture Absorption | 24hr in 23℃ | ASTM D-570 | 0.20 % |
| (23°C,24hr) | ISO62 | 0.20 % |
| Mechanical Properties | Test Condition | Test Method | TEIJIN JAPAN/LN-2250Y |
|---|---|---|---|
| Flexural Strength | 2mm/min | ISO 178 | 92 Mpa |
| 23°C | ISO178 | 92.0 Mpa | |
| ASTM D790/ISO 178 | /92 kg/cm²(MPa)[Lb/in²] | ||
| Tensile Elongation?(Break) | 屈服，23°C | ISO527-2 | 6.0 % |
| Izod Impact Strength | 带缺口 | ISO 179 | 12 KJ/m |
| Tensile Stress(Yield) | 50mm/min | ISO 527-1 and ISO 527-2 | 61 Mpa |
| Tensile Elongation?(Yield) | 6 % | ||
| Tensile Strength | ASTM D638/ISO 527 | /61 kg/cm²(MPa)[Lb/in²] | |
| Izod Impact Strength | 没缺口 | ISO 179 | NB KJ/m |
| Tensile Modulus | 23°C | ISO527-2 | 2400 Mpa |
| Notched Izod Impact Strength | ISO180/1A | 76 kJ/m² | |
| Tensile Modulus | ASTM D638/ISO 527 | /2400 kg/cm²(MPa)[Lb/in²] | |
| 1mm/min | ISO 527-1 and ISO 527-2 | 2400 Mpa | |
| Tensile Elongation | ASTM D638/ISO 527 | /6 % | |
| Tensile Elongation?(Break) | 23°C | ISO527-2 | >50 % |
| Unnotched Izod Impact Strength | ISO180/1U | NB kJ/m² | |
| Flexural Modulus | ISO178 | 2350 Mpa | |
| Tensile Elongation (Break) | 50mm/min | ISO 527-1 and ISO 527-2 | >50 % |
| Tensile Strength | 屈服，23°C | ISO527-2 | 61.0 Mpa |
| Flexural Modulus | ASTM D790/ISO 178 | /2350 kg/cm²(MPa)[Lb/in²] | |
| 2mm/min | ISO 178 | 2350 Mpa |
| Optical | Test Condition | Test Method | TEIJIN JAPAN/LN-2250Y |
|---|---|---|---|
| Index of Refraction | ASTM D542/ISO 489 | 1.585 | |
| Transmittance | ASTM D1003/ISO 13468 | 88 % |
| Physical Properties | Test Condition | Test Method | TEIJIN JAPAN/LN-2250Y |
|---|---|---|---|
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.2 % | |
| Density | ASTM D792/ISO 1183 | /1200 | |
| Modeling Shrinkage | ASTM D955 | 0.5-0.7 % |
| Flammability | Test Condition | Test Method | TEIJIN JAPAN/LN-2250Y |
|---|---|---|---|
| Fire rating | UL-94 | 0.43mm V-2 | |
| 3.00mm V-0 |
| Electrical Properties | Test Condition | Test Method | TEIJIN JAPAN/LN-2250Y |
|---|---|---|---|
| Dissipation Factor?(Tangent) | 1MHz | IEC 60250 | 90 |
| Dielectric Constant | 3 | ||
| Arc Resistance | 短时间法 | IEC 60243-1 | 32 MV/m |
| Dielectric Constant | IEC60250 | 3.00 1MHz | |
| Volume Resistivity | IEC 60093 | >1×10 Ω.cm | |
| Arc Resistance | IEC 60112 | 225 | |
| Dissipation Factor? | 相对漏电起痕指数 | IEC60112 | 225 V |
| Dielectric Constant | IEC60250 | 32 1kHz | |
| Dissipation Factor?(Tangent) | 100Hz | IEC 60250 | 10 |
| Volume Resistivity | IEC60093 | >1.0E+15 Ω.cm | |
| Dissipation Factor? | IEC60250 | 9E-03 | |
| Surface Resistivity | IEC600 | >1×10 Ω | |
| Dielectric Constant | 100Hz | IEC 60250 | 3.1 |
| ASTM D150/IEC 60250 | 3 | ||
| Surface resistance | IEC60093 | >1.0E+15 Ω.cm | |
| Dielectric Constant | IEC60250 | 3.10 100HZ |
| Processing | Test Condition | Test Method | TEIJIN JAPAN/LN-2250Y |
|---|---|---|---|
| Modeling Shrinkage | 平行方向 | 本公司制订的测定法 | 0.5～0.7 % |
| 垂直方向 | 0.5～0.7 % |