PBT VALOX™ ENH4560 BK1066 SABIC INNOVATIVE NANSHA
132
Unit Price:$7108 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜Bromine free｜Chlorine free
- Application Areas:Plastic bag｜Automotive External Parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 265°C/5.0kg | ASTMD1238 | 23 g/10min |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 16.0 cm3/10min |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Evolution Calendar intelligent importer | UL746 | 125 °C | |
| RTI | UL746 | 140 °C | |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 223 °C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 225224 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 210 °C | |
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 210 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD:-40到40°C | ISO11359-2 | 2E-05 cm/cm/°C |
| MD:23到150°C | ISO11359-2 | 2.5E-05 cm/cm/°C | |
| TD:-40到40°C | ISO11359-2 | 6.2E-05 cm/cm/°C | |
| TD:23到150°C | ISO11359-2 | 1.5E-04 cm/cm/°C | |
| RTIElec | UL746 | 140 °C |
| Additional | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Filler Content | ASTMD229 | 30 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 0.800mm | UL94 | V-0 |
| 3.00mm | UL94 | 5VB | |
| Glow Wire Flammability Index | 2.00mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | 750 °C |
| 2.00mm | IEC60695-2-13 | 750 °C | |
| 3.00mm | IEC60695-2-13 | 800 °C |
| Fill Analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 110 Pa·s |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTMD638 | 11000 Mpa | |
| Yield | ASTMD638 | 110 Mpa | |
| yield | ISO527-2/5 | 105 Mpa | |
| Break | ASTMD638 | 110 Mpa | |
| Flexural Strain (Break) | ISO178 | 2.0 % | |
| fracture | ISO527-2/5 | 105 Mpa | |
| Yield | ASTMD638 | 2.0 % | |
| yield | ISO527-2/5 | 2.0 % | |
| Break | ASTMD638 | 2.0 % | |
| fracture | ISO527-2/5 | 2.0 % | |
| 50.0mm Span | ASTMD790 | 9000 Mpa | |
| --7 | ISO178 | 10000 Mpa | |
| --8 | ISO178 | 170 Mpa | |
| Yield,50.0mm Span | ASTMD790 | 150 Mpa | |
| Break,50.0mm Span | ASTMD790 | 150 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dielectric Constant | 1MHz | ASTMD150,IEC60250 | 3.80 |
| Dissipation Factor? | 1MHz | ASTMD150,IEC60250 | 0.14 |
| Comparative Tracking Index | CTI | UL746 | PLC 0 |
| IEC60112 | 600 V | ||
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| Hot-wire Ignition | HWI | UL746 | PLC 0 |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Volume Resistivity | ASTMD257,IEC60093 | 1E+14 ohms·cm | |
| 0.800mm,inOil | ASTMD149 | 32 KV/mm | |
| 1.60mm,inOil | ASTMD149 | 22 KV/mm | |
| 3.20mm,inOil | ASTMD149 | 18 KV/mm | |
| 0.800mm, in oil | IEC60243-1 | 32 KV/mm | |
| 1.60mm,in Oil | IEC60243-1 | 22 KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 18 KV/mm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R计秤 | ISO2039-2 | 120 |
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 142 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C14 | ISO180/1A | 9.0 kJ/m² | |
| -30°C | ASTMD4812 | 500 J/m | |
| 23°C | ASTMD4812 | 500 J/m | |
| -30°C15 | ISO180/1U | 37 kJ/m² | |
| 23°C16 | ISO180/1U | 37 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/2U | 35 kJ/m² |
| 23°C | ISO179/2U | 40 kJ/m² | |
| -30°C | ASTMD256 | 75 J/m | |
| 0°C | ASTMD256 | 75 J/m | |
| 23°C | ASTMD256 | 75 J/m | |
| -30°C12 | ISO180/1A | 9.0 kJ/m² | |
| 0°C13 | ISO180/1A | 9.0 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.