Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT ENH4560 BK1066 SABIC INNOVATIVE NANSHA
VALOX™
Plastic bag、Automotive External Parts
Flame retardant、Bromine free、Chlorine free
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 210 °C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 225224 °C | |
| Linear thermal expansion coefficient | MD:23到150°C | ISO11359-2 | 2.5E-05 cm/cm/°C |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 210 °C | |
| RTIElec | UL746 | 140 °C | |
| Linear thermal expansion coefficient | TD:23到150°C | ISO11359-2 | 1.5E-04 cm/cm/°C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD:-40到40°C | ISO11359-2 | 2E-05 cm/cm/°C |
| RTI | UL746 | 140 °C | |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 223 °C | |
| Linear thermal expansion coefficient | TD:-40到40°C | ISO11359-2 | 6.2E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 125 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 142 Mpa |
| Rockwell Hardness | R计秤 | ISO2039-2 | 120 |
| Fill Analysis | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 110 Pa·s |
| Additional | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| Filler Content | ASTMD229 | 30 % |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 16.0 cm3/10min |
| Melt Mass-Flow Rate | 265°C/5.0kg | ASTMD1238 | 23 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| Break | ASTMD638 | 110 Mpa | |
| yield | ISO527-2/5 | 2.0 % | |
| Yield,50.0mm Span | ASTMD790 | 150 Mpa | |
| yield | ISO527-2/5 | 105 Mpa | |
| fracture | ISO527-2/5 | 2.0 % | |
| ISO178 | 170 Mpa | ||
| Break,50.0mm Span | ASTMD790 | 150 Mpa | |
| ASTMD638 | 11000 Mpa | ||
| fracture | ISO527-2/5 | 105 Mpa | |
| Break | ASTMD638 | 2.0 % | |
| Flexural Strain (Break) | ISO178 | 2.0 % | |
| Yield | ASTMD638 | 2.0 % | |
| 50.0mm Span | ASTMD790 | 9000 Mpa | |
| Yield | ASTMD638 | 110 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/2U | 40 kJ/m² |
| ASTMD256 | 75 J/m | ||
| ASTMD4812 | 500 J/m | ||
| Charpy Unnotched Impact Strength | -30°C | ISO179/2U | 35 kJ/m² |
| ISO180/1A | 9.0 kJ/m² | ||
| ISO180/1U | 37 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| Flame Rating | 0.800mm | UL94 | V-0 |
| Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | 750 °C |
| Glow Wire Flammability Index | 2.00mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 3.00mm | IEC60695-2-13 | 800 °C |
| Flame Rating | 3.00mm | UL94 | 5VB |
| Glow Wire Ignition Temperature | 2.00mm | IEC60695-2-13 | 750 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ENH4560 BK1066 |
|---|---|---|---|
| Dielectric Constant | 1MHz | ASTMD150,IEC60250 | 3.80 |
| ASTMD149 | 18 KV/mm | ||
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| 3.20mm,in Oil | IEC60243-1 | 18 KV/mm | |
| Comparative Tracking Index | IEC60112 | 600 V | |
| 0.800mm, in oil | IEC60243-1 | 32 KV/mm | |
| Dissipation Factor? | 1MHz | ASTMD150,IEC60250 | 0.14 |
| 1.60mm,in Oil | IEC60243-1 | 22 KV/mm | |
| Volume Resistivity | ASTMD257,IEC60093 | 1E+14 ohms·cm | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Hot-wire Ignition | HWI | UL746 | PLC 0 |
| Comparative Tracking Index | CTI | UL746 | PLC 0 |