ASA STAREX® WR-9300HF Samsung Cheil South Korea

125

Unit Price:$1917 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 31MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance High temperature resistan
Application Areas:Electronic and electrical Automotive components
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt mass flow rate	220°C/10.0kg	ASTMD1238	12	g/10min
	Melt mass flow rate	250°C/2.16kg	ASTMD1238	6.5	g/10min
		Melt mass flow rate	220°C/10.0kg	ISO1133	12	g/10min
		Melt mass flow rate	Melt mass flow rate	250°C/2.16kg	ISO1133	6.5	g/10min
Shrinkage rate	MD：3.20mm	ASTMD955	0.40to0.70	%
	Shrinkage rate	TD：3.20mm	ASTMD955	0.40to0.70	%
		Shrinkage rate	TD:3.20mm	ISO2577	0.40to0.70	%
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO2577	0.40to0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
tensile strength	Yield	ASTMD638	44.1	Mpa
tensile strength	tensile strength	Yield	ISO527-2/5	44.0	Mpa
elongation	Break	ASTMD638	15	%
Bending modulus		ASTMD790	2160	Mpa
Bending modulus	Bending modulus		ISO178	2100	Mpa
Bending strength		ASTMD790	66.7	Mpa
Bending strength	bending strength		ISO178	67.0	Mpa
CharpyNotchedImpactStrength	23°C	ISO179/1eA	13	kJ/m²
Suspended wall beam gap impact strength	-30°C	ISO180/1A	5.5	kJ/m²
Suspended wall beam gap impact strength	Suspended wall beam gap impact strength	23°C	ISO180/1A	12	kJ/m²
Rockwell hardness	R-Scale	ASTMD785	106
Rockwell hardness	Rockwell hardness	R-Scale	ISO2039-2	106

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTMD648	86.0	°C
	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTMD648	92.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTMD648	73.0	°C
			Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTMD648	87.0	°C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO75-2/A	80.0	°C
vicat softening point		ISO306/B50	100	°C

optical performance	Test Condition	Test Method	Test Result	Unit
Huangdu Index	3.20mm	ASTMD1925	25	YI

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.