Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA WR-9300HF Samsung Cheil South Korea
STAREX®
Electronic and electrical、Automotive components
UV resistance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ASA/Samsung Cheil South Korea/WR-9300HF
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
1
Melt mass flow rate
250°C/2.16kg
ASTMD1238
g/10min
6
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
1
Melt mass flow rate
250°C/2.16kg
ISO1133
g/10min
6
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD:3.20mm
ISO2577
%
0
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
ASA/Samsung Cheil South Korea/WR-9300HF
CharpyNotchedImpactStrength
23°C
ISO179/1eA
kJ/m²
1
tensile strength
屈服
ASTMD638
Mpa
4
tensile strength
屈服
ISO527-2/5
Mpa
4
elongation
断裂
ASTMD638
%
1
Bending modulus
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
Bending strength
ASTMD790
Mpa
6
bending strength
ISO178
Mpa
6
Suspended wall beam gap impact strength
-30°C
ISO180/1A
kJ/m²
5
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
ASA/Samsung Cheil South Korea/WR-9300HF
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
8
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
8
vicat softening point
ISO306/B50
°C
1
optical performance
Test Condition
Test Method
Unit
ASA/Samsung Cheil South Korea/WR-9300HF
Huangdu Index
3.20mm
ASTMD1925
YI
2